Highly textured Nd–Fe–B films grown on amorphous substrates

Abstract Thin films with an almost perfect alignment of Nd 2 Fe 14 B grains with the c -axis (easy magnetisation direction) perpendicular to the film plane were achieved on amorphous SiN substrates using pulsed laser deposition. The texture arises due to epitaxial growth on a Ta(1 1 0) buffer deposited prior to the Nd–Fe–B film. Out-of-plane coercivity of 1.3 T and remanence to saturation magnetisation ratio around 0.95 are obtained for Nd-rich films. An analysis of the coercivity mechanism shows that the switching mechanism is nucleation dominated, independent of the Nd content.