Effect of nanocrystalline particles on the magnetic properties of Z-type hexaferrites

Abstract In order to improve the magnetic properties of Z-type hexaferrites such as high initial permeability and high-quality factor, the nanocrystalline hexaferrite particles (NHPs) with the same chemical composition were introduced. The influence of NHPs on the densification, microstructures and magnetic properties of the ceramics prepared by a combined method was investigated. The results show that these NHPs, which spread around the micron-sized hexaferrite particles (MHPs), enhance the densification by increasing the inter-diffusion of the particles due to the increase of contact area; simultaneously, the grain growth in the direction of c -plane is dominant. Due to the special microstructure, high sintering density, and no addition sintering aids with different chemical composition, relatively high initial permeability and Q -factor than those of the samples with 1.0 wt% Bi 2 O 3 were obtained in the samples with proper nanocrystalline particles sintered at 900 °C.