Optimisation of soft magnetic properties in Fe–Cu–X–Si13B9 (X=Cr, Mo, Zr) amorphous alloys

Abstract In the present paper a group of Fe–Cu–X–Si 13 B 9 (X=Cr, Mo, Zr) amorphous alloys has been examined by applying different experimental techniques—magnetic permeability, magnetic after-effect, coercive force and electrical resistivity measurements. It has been shown that their soft magnetic properties can be optimised by 1-h thermal annealing at the temperature close to the crystallisation temperature. This leads to an increase of permeability and a decrease of coercive force, thermal instability (magnetic after-effect intensity) and electrical resistivity of the material. The optimisation effect is discussed in terms of different processes—(i) a formation of a nanocrystalline phase with the grain size much smaller than the ferromagnetic exchange length, (ii) an annealing out of microvoids formed during the fabrication process and also (iii) a decrease of the effective magnetostriction constant. The temperature of optimisation annealing treatment is always higher than the Curie temperatures of the materials and varies approximately linearly with the atomic radius of the alloying additions.