Observation of the magnetization-step in Gd doped antiperovskite compounds Mn3Cu1−xGdxN (0.15≤x≤0.25)
Source abstract
Abstract
Abstract (Gadolinium) Gd-doped antiperovskite compounds Mn 3 Cu 1−x Gd x N were synthesized by the conventional solid-state reaction. With increasing Gd concentration, two magnetic transitions appeared at a high Curie temperature (T C1 ) corresponding to paramagnetic (PM)-ferromagnetic (FM) transition and a low temperature (T C2 ) ascribed to the FM-antiferromagnetic (AFM) transition. The magnetic relaxation results show the formation of a magnetic metastable state after the FM-AFM transition at low temperature (lower than T C2 ), forming a novel magnetic-step feature in the process from AFM to FM under a certain magnetic field.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Thermal Expansion and Ionic Conductivity · Advanced Battery Materials and Technologies · Ferroelectric and Piezoelectric Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (55)
Show source-provided references
1. Kan · J. Alloy. Compd. · 2016 · 663 · 9410.1016/j.jallcom.2015.12.156 ↗
2. Lin · J. Alloy. Compd. · 2013 · 572 · 14510.1016/j.jallcom.2013.03.090 ↗
3. Lin · J. Alloy. Compd. · 2013 · 551 · 59110.1016/j.jallcom.2012.10.146 ↗
4. Xing · J. Alloy. Compd. · 2003 · 360 · 28610.1016/S0925-8388(03)00345-1 ↗
5. Guo · Appl. Phys. Lett. · 2015 · 107 · 20240610.1063/1.4936239 ↗
6. Sun · Inorg. Chem. · 2013 · 52 · 80010.1021/ic3019265 ↗
7. Deng · Chem. Mater. · 2015 · 27 · 249510.1021/cm504702m ↗
8. Chen · Cryo · 2012 · 52 · 62910.1016/j.cryogenics.2012.08.009 ↗
9. Zhang · J. Appl. Phys. · 2014 · 115 · 12390510.1063/1.4869797 ↗
10. Wang · Appl. Phys. Lett. · 2009 · 95 · 22250910.1063/1.3268786 ↗
11. Asano · Appl. Phys. Lett. · 2008 · 92 · 16190910.1063/1.2917472 ↗
12. Song · Appl. Phys. Lett. · 2008 · 92 · 19251110.1063/1.2931058 ↗
13. Ding · J. Appl. Phys. · 2015 · 117 · 21391510.1063/1.4921537 ↗
14. Tan · J. Alloy. Compd. · 2014 · 593 · 10310.1016/j.jallcom.2014.01.027 ↗
15. Sun · Appl. Phys. Lett. · 2007 · 91 · 23191310.1063/1.2822813 ↗
16. Hamada · J. Appl. Phys. · 2011 · 109 · 07E30910.1063/1.3540604 ↗
17. Sun · J. Am. Ceram. Soc. · 2010 · 93 · 65010.1111/j.1551-2916.2009.03482.x ↗
18. Wang · Phys. Rev. B · 2012 · 85
19. Huang · Solid State Sci. · 2010 · 12 · 197710.1016/j.solidstatesciences.2010.08.010 ↗
20. Lin · Appl. Phys. Lett. · 2015 · 106 · 08240510.1063/1.4913663 ↗
21. Lin · Appl. Phys. Lett. · 2015 · 107 · 13190210.1063/1.4932067 ↗
22. Yan · Acta Mater. · 2014 · 74 · 5810.1016/j.actamat.2014.04.005 ↗
23. Iikubo · Phys. Rev. B · 2008 · 7710.1103/PhysRevB.77.020409 ↗
24. Chen · Chem. Soc. Rev. · 2015 · 44 · 352210.1039/C4CS00461B ↗
25. Chen · Phys. Rev. Lett. · 2013 · 110 · 11590110.1103/PhysRevLett.110.115901 ↗
26. Sun · Solid State Commun. · 2012 · 152 · 44610.1016/j.ssc.2012.01.011 ↗
27. Shi · Adv. Mater. · 2016 · 28 · 376110.1002/adma.201600310 ↗
28. Matsunami · Nat. Mater. · 2015 · 14 · 7310.1038/nmat4117 ↗
29. Chi · Solid State Commun. · 2001 · 120 · 30710.1016/S0038-1098(01)00395-7 ↗
30. Huang · Solid State Commun. · 2010 · 150 · 161710.1016/j.ssc.2010.06.041 ↗
31. Zhang · Appl. Phys. Lett. · 2013 · 103 · 02240510.1063/1.4813412 ↗
32. Huang · Appl. Phys. Lett. · 2008 · 93 · 08190210.1063/1.2970998 ↗
33. Song · Adv. Mater. · 2011 · 23 · 469010.1002/adma.201102552 ↗
34. Huang · Cryo · 2010 · 50 · 75010.1016/j.cryogenics.2010.09.001 ↗
35. Ding · Appl. Phys. Lett. · 2011 · 99 · 25190510.1063/1.3671183 ↗
36. Lin · Scr. Mater. · 2011 · 65 · 45210.1016/j.scriptamat.2011.05.035 ↗
37. Chen · Appl. Phys. Lett. · 2006 · 89 · 10191410.1063/1.2347279 ↗
38. Chen · Appl. Phys. Lett. · 2007 · 91 · 17190710.1063/1.2794742 ↗
39. Chen · J. Am. Chem. Soc. · 2008 · 4 · 114410.1021/ja7100278 ↗
40. Chen · J. Am. Chem. Soc. · 2011 · 133 · 1111410.1021/ja2046292 ↗
41. Sun · Inorg. Chem. · 2012 · 51 · 723210.1021/ic300978x ↗
42. Lin · Appl. Phys. Lett. · 2011 · 98 · 09250710.1063/1.3562315 ↗
43. Shibayama · J. Appl. Phys. · 2011 · 109 · 07A92810.1063/1.3560892 ↗
44. Lin · Sci. Rep. · 2015 · 5 · 793310.1038/srep07933 ↗
45. Takenaka · Appl. Phys. Lett. · 2009 · 95 · 13250810.1063/1.3243340 ↗
46. Takenaka · Sci. Technol. Adv. Mater. · 2016 · 15 · 01500910.1088/1468-6996/15/1/015009 ↗
47. Cao · Appl. Phys. Lett. · 2005 · 86 · 04250710.1063/1.1852710 ↗
48. Nair · J. Appl. Phys. · 2014 · 116 · 12390710.1063/1.4896399 ↗
49. Mahendiran · Phys. Rev. Lett. · 2002 · 89 · 28660210.1103/PhysRevLett.89.286602 ↗
50. Wu · Phys. Rev. B · 2004 · 69
51. Zhu · Solid State Commun. · 2007 · 144 · 7810.1016/j.ssc.2007.08.003 ↗
52. Levin · Phys. Rev. B · 2002 · 6510.1103/PhysRevB.65.214427 ↗
53. Li · J. Alloy. Compd. · 2011 · 509 · 265410.1016/j.jallcom.2010.11.182 ↗
54. Roy · Phys. Rev. B · 2005 · 71
55. Lin · J. Appl. Phys. · 2012 · 111 · 11391410.1063/1.4725471 ↗