Room temperature deposition of perpendicular magnetic anisotropic Co3Pt thin films on glass substrate

Abstract Co 3 Pt alloy thin films were deposited on the glass substrate at room temperature ( RT ) and 300 °C, which showed high perpendicular magnetic anisotropy (PMA) and isotropy magnetic behaviors, respectively. Co 3 Pt HCP (0002) planes grew along the substrate plane for the films deposited at RT . The easy axis [0001] was consequently vertical to the substrate surface and obtained the predominant PMA. Large magnetic domains and sharp boundary also supported high PMA in RT -deposited samples. On the other hand, the PMA was significantly decreased with increasing the deposition temperature from RT to 300 °C. Hard HCP(0002) and soft A 1(111) co-existed in the film and the magnetic exchanged coupling between these two phases induced isotropy magnetic behavior. In addition, the various thicknesses ( t ) of the RT -deposited Co 3 Pt films were deposited with different base pressures prior to sputtering. The Kerr rotation loops showed high PMA and out-of-plane squareness ( S ⊥ ) of ~0.9 were found in low base pressure chamber. Within high base pressure chamber, Co 3 Pt films just show magnetic isotropy behaviors. This study provides a fabrication method for the preparation of high PMA HCP-type Co 3 Pt films on the glass substrate without any underlayer at RT . The results could be the base for future development of RT- deposited magnetic alloy thin film with high PMA.