Reproduced multi-domain regions during demagnetization in Nd2Fe14B sintered magnets with different average grain sizes
Source abstract
Abstract
Abstract We prepared five Nd2Fe14B sintered magnets with similar saturation polarizations (Js) of 1.38–1.43 T and anisotropy fields (Ha) of 6.76–8.52 T, but different grain sizes (DAV) of 3.1–8.4 μm in diameter and obviously different coercivities (μ0Hc) of 0.8–1.6 T. The observed difference in coercivity could not be explained by the Kronmuller equation, because of the similar Ha values and similar chemical compositions and microstructures resulting from similar preparation method except DAV. The Hc values themselves, however, are inversely proportional to DAV. During demagnetization after magnetization in a 5 T pulse field, domain wall motion (DWM) was observed except in the sample with μ0Hc = 1.6 T by using our step method. The DWM was also confirmed by susceptibility measurements using a custom-built vibrating sample magnetometer, and DWM was generated in the reproduced multi-domain regions (RMDR) during demagnetization. The magnitude of DWM as a polarization change in the RMDR was inversely proportional to the coercivities of the samples. Therefore, it should be considered that the propagation of the nucleated region through the grain boundary, which corresponds to the expansion process in previous studies, was different caused by, first, the difference in DAV, and, second, in grain boundary state which was varied by difference in final annealing temperature.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnetic Properties of Alloys · Magnetic Properties and Applications · Magnetic properties of thin films
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (15)
Show source-provided references
1. Magnetic viscosity and thermal activation energy10.1063/1.336671 ↗
2. Coercivity
3. Ferromagnetic domain wall pinning by a random array of inhomogeneities10.1080/13642818308228288 ↗
4. H. Zijlstra, “Permanent Magnets; Theory”, Chap.2, in: E.P. Wohlfarth (Ed.), Ferromagnetic Materials (North-Holland), 1982, pp.37–105.10.1016/S1574-9304(05)80088-4 ↗
5. The coercive field of sintered and melt-spun NdFeB magnets10.1016/0304-8853(87)90097-7 ↗
6. Analysis of the magnetic hardening mechanism in RE-FeB permanent magnets10.1016/0304-8853(88)90202-8 ↗
7. Reduction in coercive force caused by a certain type of imperfection10.1103/PhysRev.119.127 ↗
8. Theory of nucleation fields in inhomogeneous ferromagnets10.1002/pssb.2221440134 ↗
9. Magnetic properties of the surface layer and its magnetic interaction with the interior of Nd-Fe-B sintered magnet10.1063/1.4919812 ↗
10. the origin of unique initial magnetization curves in Dy-substituted (Nd1-x, Dyx)2Fe14B (x=0-1) sintered magnets10.1063/1.3676209 ↗
11. The origin of coercivity enhancement in newly prepared high coercivity Dy-free Nd-Fe-B sintered magnet10.1063/1.4803131 ↗
12. Magnetic properties and domain structures in Nd–Fe–B sintered magnets with Tb additive reacted and diffused from the sample surface10.1016/j.jallcom.2014.06.170 ↗
13. Effects of crystal anisotropy, grain and domain sizes on coercivity mechanism of the Nd-Fe-B sintered magnets10.2320/jinstmet.76.27 ↗
14. Magnetization mechanism and coercivity in rare-earth magnets
15. The influence of planar defects on the coercive field of hard magnetic materials10.1007/BF00915199 ↗