In-plane magnetization with high coercivity in terbium iron garnet thin films deposited on Pt/Si substrate by PLD

Abstract We report on the growth of terbium iron garnet (TbIG, Tb 3 Fe 5 O 12 ) thin films having anomalously large coercivity and in-plane easy axis of magnetization. The TbIG thin films were prepared at room temperature (RT) on Pt/Si(1 0 0) substrates by pulsed laser deposition technique. The films deposited at RT were X-ray amorphous and do not show any magnetic order. Annealing of the RT deposited film at 900 °C resulted into fully textured (532) TbIG film. Atomic force microscopy and cross-sectional scanning electron microscopy studies of the TbIG films showed good surface quality with an average surface roughness of 5.0 nm and thickness of about 300 nm, respectively. The M – H loops measured at 20 K for TbIG films, exhibit about an order of magnitude enhancement in the coercivity value ( H c ) than the single crystal. In-plane and out-of-plane M – H loops revealed that the easy axis of the magnetization lies within the film’s plane. In-plane magnetization combining with large H c value of the TbIG thin film may be of scientific interest for the possible applications.