Antiferromagnetic Mn50Fe50 wire with large magnetostriction

Abstract This work presents a study on the relation between the fiber texture and the magnetostrictive performance in an antiferromagnetic Mn 50 Fe 50 alloy wire, which was prepared through the combining process of hot rolling and cold drawing. The face-centered cubic (fcc) crystal structure can be retained during the plastic deformation process. Mixed fiber textures consisting of both 〈1 1 0〉 and 〈1 0 0〉 components were formed along the drawing direction (DD) in the wire. A large magnetostriction of 750 ppm was obtained along DD under 1.2 T, which can be ascribed to the single γ phase and the formation of preferred crystal orientation.