Optimization of spin-valve parameters for magnetic bead trapping and manipulation

Abstract Magneto-optic Kerr effect (MOKE) and magnetoresistance (MR) measurements were used to measure the switching characteristics of spin-valve (SV) arrays currently being developed to trap and release superparamagnetic beads within a fluid medium. The effect of SV size on switching observed by MOKE showed that a 1 μm×8 μm SV element was found to have optimal switching characteristics. MR measurements on a single 1 μm×8 μm SV switched with either an external applied magnetic field or a local magnetic field generated by an integrated write wire (current density ranging from 10 6 to 10 7 A/cm 2 ) confirmed the MOKE findings. The 1 μm×8 μm SV low field switching was observed to be +8 and −2 mT with two stable states at zero field; the high field switching was observed to be −18 mT. The low switching fields and the large magnetic moment of the SV trap along with our observation of minimal magnetostatic effects for dense arrays are necessary design characteristics for high-force, “switchable-magnet,” microfluidic bead trap applications.