Pt diffusion driven L1 0 ordering in off-stoichiometric FePt thin films

Abstract Pt/Fe 3 Pt thin films were deposited on the 〈100〉 silicon substrates at room temperature using DC sputtering. As-deposited Pt (25 nm)/Fe 3 Pt (70 nm) bilayers were subjected to heat treatment and a systematic study was carried out to investigate the structural and magnetic phase transition as a function of annealing temperature. The as-obtained films show an A1 disordered, face centered cubic phase which exhibit a magnetically soft behavior. After annealing at 300 °C for 1 h, the set in of L1 0 face centered tetragonal phase was observed and is attributed to the atomic diffusion at Pt/Fe 3 Pt interface. A coercivity of 6.8 kOe was obtained for Pt/Fe 3 Pt at 300 °C which increases to 12.5 kOe at 400 °C due to enhanced fct phase formation. Rutherford back scattering study has also been performed to investigate the inter-layer diffusion of Fe 3 Pt and Pt, along with estimation of film thickness and atomic composition with annealing temperature. The thickness and composition of films annealed at 600 °C was found to be 73 nm and Fe 54 Pt 46 , respectively. Lower temperature ordering is achieved for these bilayer films.