The effect of cooling rate on the phase formation and magnetocaloric properties in La0.6Ce0.4Fe11.0Si2.0 alloys

Abstract In this work, the microstructure, phase formation behavior of the NaZn13-type 1:13 phase and related magnetocaloric effect have been investigated in La0.6Ce0.4Fe11.0Si2.0 as-cast bulk and melt-spun ribbons with different cooling rates. A multi-phase structure consisting of 1:13, α-Fe and La-rich phases is observed in the induction-melted sample with slow cooling. By fast cooling in the melt spinning processing, the La-rich phase can be almost eliminated and thus 1:13 phases with volume fraction as high as 74.4% directly form in the absence of further heat treatment. The resulting maximum magnetic entropy change of 3.1 J/kg K in 2 T field appears at its Curie temperature of 210 K for the La0.6Ce0.4Fe11.0Si2.0 ribbon prepared in 25 m/s.