Epitaxial growth of bcc–FexCo100-x thin films on MgO(110) single-crystal substrates

Abstract Fe x Co 100– x ( x =100, 65, 50 at%) epitaxial thin films were prepared on MgO(1 1 0) single-crystal substrates heated at 300 °C by ultra-high vacuum molecular beam epitaxy. The film structure and the growth mechanism are discussed. FeCo(2 1 1) films with bcc structure grow epitaxially on MgO(1 1 0) substrates with two types of variants whose orientations are rotated around the film normal by 180° each other for all compositions. Fe x Co 100– x film growth follows the Volmer Weber mode. X-ray diffraction analysis indicates the out-of-plane and the in-plane lattice spacings are in agreement with the values of respective bulk Fe x Co 100– x crystals with very small errors less than ±0.4%, suggesting the strains in the films are very small. High-resolution cross-sectional transmission electron microscopy shows that periodical misfit dislocations are preferentially introduced in the film at the Fe 50 Co 50 /MgO interface along the MgO[1 1¯ 0] direction. The presence of such periodical dislocations decreases the large lattice mismatch of about −17% existing at the FeCo/MgO interface along the MgO[1 1¯ 0] direction.