Effect of composition on phase formation, microstructure and magnetic properties of Nd–Fe–B thin films

Abstract Nd–Fe–B hard magnetic thin films were deposited on a combined Cr/Ta buffer layer on heated MgO(1 0 0) substrates by pulsed laser deposition. The effect of composition on phase formation, morphology and magnetic properties was investigated. For a quantification of phase formation, hysteresis measurements along the hard axis are used. Optimum phase formation is obtained at a Nd/Fe ratio around 0.3. For this Nd content an excellent magnetic texture and a coercivity up to 1 T can be obtained; however, remanence is reduced and the films have a granular microstructure with high roughness. Also a certain B surplus is of benefit. However, with a too-high B or Nd surplus phase formation is more difficult.