Magnetic properties of doped ZnO prepared by different synthetic routes

Abstract We have studied the magnetic properties of Zn 0.96 M 0.04 O (M=Mn, Fe, Co) compounds prepared using several routes. The low temperature ceramic synthesis gave multiphasic samples and show ferromagnetic behavior. Single phases can be obtained by heating at higher temperatures (∼900–1100 °C). The use of very low oxygen pressure also favours the preparation of single-phases. We were also successful in preparing single-phase samples at very low temperature (∼400 °C) by using a sol-gel method. All of the samples without noticeable secondary phases in the X-ray patterns behave as conventional paramagnets. This is true even for the samples with very low grain size. Samples exhibiting secondary phases reveal spontaneous magnetization even at room temperature in some cases. Our results strongly support that ferromagnetism at room temperature is always due to the presence of secondary phases and not to the doping of ZnO.