Preparation of magnetic latexes functionalized with chloromethyl groups via emulsifier-free miniemulsion polymerization

Abstract Functionalized crosslinked polystyrene-co-divinylbenzene-co-chloromethylstyrene magnetic latex particles were prepared via emulsifier-free miniemulsion polymerization using 2, 2′ azobis (2-amidinopropane) dihydrochloride (V-50) as an initiator and in the presence of magnetite nanoparticles in the monomers. Transmission electron microscopy (TEM) proved the presence of magnetite nanoparticles in polymer particles. Differential scanning calorimetery (DSC) analysis of the product showed an exothermic signal due to crosslinking of chains through electrophilic aromatic substitution of phenyl groups with chloromethyl groups in the presence of the dispersed Fe 3 O 4 as Lewis acid. This was proven by thermogravimetric analysis (TGA) via the loss of gaseous HCl. The results were also compared with those of magnetite-free miniemulsion polymerization using V-50.