On the relation between the effective ferromagnetic resonance linewidth Δfeff and damping parameter αeff in ferromagnetic Fe–Co–Hf–N nanocomposite films

Abstract Ferromagnetic Fe–Co–Hf–N nanocomposite films were investigated concerning their microstructure-dependent frequency behaviour. To modify the composition, the films were deposited by reactive RF magnetron sputtering by using three different 6 in. targets with various Hf fractions. The films were post-annealed up to 600 °C in a static magnetic field to induce an in-plane uniaxial anisotropy and to obtain different crystal sizes. Depending on the annealing temperature, high-frequency losses were investigated by considering the full-width at half-maximum (FWHM) Δ f eff of the imaginary part of the frequency-dependent permeability which showed a resonance frequency f FMR of 2.3 GHz for an in-plane uniaxial anisotropy field H u of 4 mT. The FWHM in correlation with the damping parameter α eff is discussed, e.g., in terms of two-magnon scattering. Damping occurs due to film inhomogeneity in magnetisation and uniaxial anisotropy caused by a magnetocrystalline anisotropy H a and/or non-magnetic phases. This will result in homogenous or even inhomogeneous resonance line broadening if additional and resonance as well as precession frequencies of independent grains arise.