Investigations of synergistic effect of surfactants as corrosion inhibitor on steel
Source abstract
Abstract
The inhibition performances of the inhibitors C8TAB-MP (a mixture of octyltrimethylammonium bromide (C8TAB) and 4-mercaptopyridine (4MP)), C8TAB and 4MP toward A3 steel in 0.5 M hydrochloric acid solution were studied at 25°C. The studied inhibitors worked in a hybrid form, mainly controlling the cathodic reaction. Their adsorption follows the Langmuir isotherm, and the compositional combination is superior to the sum of their individual properties. The highest inhibition efficiency of C8TAB-MP was 99.4% at a concentration of 200 mg/l. The surface morphologies of samples were obtained from atomic force microscopy tests. The synergistic effect between C8TAB and 4MP was due to the C8TAB molecules donating electrons and the 4MP molecules accepting electrons.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Concrete Corrosion and Durability · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Materials Science and Engineering, China University of Mining and Technology (Beijing), Beijing, China
Materials and Structural Engineering Department, Nanjing Hydraulic Research Institute, Nanjing, China
Department of Materials Science and Engineering, Beijing Key Laboratory of Failure, Corrosion and Protection of Oil/Gas Facilities, China University of Petroleum (Beijing), Beijing, China
epartment of Mechanical Engineering, University of Alaska Fairbanks, Fairbanks, AK, USA
References (56)
Show source-provided references
1. 10.1038/s41529-017-0005-210.1038/s41529-017-0005-2 ↗
2. 10.1016/j.matlet.2018.10.17710.1016/j.matlet.2018.10.177 ↗
3. 10.1016/j.matlet.2018.06.10810.1016/j.matlet.2018.06.108 ↗
4. 10.1021/jp056066410.1021/jp0560664 ↗
5. 10.1016/j.matlet.2021.13124910.1016/j.matlet.2021.131249 ↗
6. 10.1021/acs.jpcc.0c0355910.1021/acs.jpcc.0c03559 ↗
7. 10.1016/j.matlet.2021.12973510.1016/j.matlet.2021.129735 ↗
8. 10.1002/cjce.2419410.1002/cjce.24194 ↗
9. 10.1002/cjce.2304210.1002/cjce.23042 ↗
10. 10.1016/j.corsci.2016.07.00610.1016/j.corsci.2016.07.006 ↗
11. 10.1016/j.corsci.2013.08.02510.1016/j.corsci.2013.08.025 ↗
12. 10.1016/j.corsci.2014.11.00710.1016/j.corsci.2014.11.007 ↗
13. 10.1016/j.corsci.2014.11.03510.1016/j.corsci.2014.11.035 ↗
14. 10.1016/j.surfcoat.2015.10.07510.1016/j.surfcoat.2015.10.075 ↗
15. 10.1038/srep3330510.1038/srep33305 ↗
16. 10.1016/j.corsci.2016.07.01810.1016/j.corsci.2016.07.018 ↗
17. 10.1016/j.jcis.2007.01.03810.1016/j.jcis.2007.01.038 ↗
18. 10.1016/j.corsci.2008.11.01310.1016/j.corsci.2008.11.013 ↗
19. 10.1021/acssuschemeng.5b0172510.1021/acssuschemeng.5b01725 ↗
20. 10.1016/j.corsci.2007.07.01010.1016/j.corsci.2007.07.010 ↗
21. 10.1016/j.molliq.2016.01.08710.1016/j.molliq.2016.01.087 ↗
22. 10.1016/j.corsci.2010.02.01810.1016/j.corsci.2010.02.018 ↗
23. 10.1006/jcis.2000.736410.1006/jcis.2000.7364 ↗
24. 10.1016/j.minpro.2008.06.00610.1016/j.minpro.2008.06.006 ↗
25. 10.1016/j.susc.2005.06.00510.1016/j.susc.2005.06.005 ↗
26. 10.1021/la049903m10.1021/la049903m ↗
27. 10.1021/la980031w10.1021/la980031w ↗
28. 10.1016/j.corsci.2009.10.01610.1016/j.corsci.2009.10.016 ↗
29. 10.1016/j.molliq.2016.03.04910.1016/j.molliq.2016.03.049 ↗
30. 10.1039/C4CP05096G10.1039/C4CP05096G ↗
31. 10.1016/j.applthermaleng.2016.08.15410.1016/j.applthermaleng.2016.08.154 ↗
32. 10.1016/j.jpowsour.2014.11.10510.1016/j.jpowsour.2014.11.105 ↗
33. 10.1016/j.surfcoat.2016.06.01510.1016/j.surfcoat.2016.06.015 ↗
34. 10.1134/S207020510905024410.1134/S2070205109050244 ↗
35. 10.1016/j.jece.2014.03.02410.1016/j.jece.2014.03.024 ↗
36. 10.1016/j.memsci.2015.12.00710.1016/j.memsci.2015.12.007 ↗
37. 10.1016/j.jcis.2016.11.04810.1016/j.jcis.2016.11.048 ↗
38. 10.1016/j.corsci.2018.05.01810.1016/j.corsci.2018.05.018 ↗
39. 10.1007/s12274-014-0601-110.1007/s12274-014-0601-1 ↗
40. 10.1021/ie402547m10.1021/ie402547m ↗
41. 10.1007/s10008-019-04408-010.1007/s10008-019-04408-0 ↗
42. 10.1016/j.cej.2008.01.02010.1016/j.cej.2008.01.020 ↗
43. 10.1016/j.molliq.2018.07.08710.1016/j.molliq.2018.07.087 ↗
44. 10.1016/j.corsci.2015.02.01010.1016/j.corsci.2015.02.010 ↗
45. 10.1038/ncomms1445710.1038/ncomms14457 ↗
46. 10.1016/j.corsci.2013.10.00910.1016/j.corsci.2013.10.009 ↗
47. 10.1016/j.corsci.2015.01.03710.1016/j.corsci.2015.01.037 ↗
48. 10.1016/j.matchemphys.2018.04.06910.1016/j.matchemphys.2018.04.069 ↗
49. 10.1149/2.0091609jes10.1149/2.0091609jes ↗
50. 10.1039/c3ee44189j10.1039/c3ee44189j ↗
51. 10.1002/anie.20110017010.1002/anie.201100170 ↗
52. 10.1016/j.jiec.2017.01.02510.1016/j.jiec.2017.01.025 ↗
53. 10.1016/j.jiec.2015.03.02810.1016/j.jiec.2015.03.028 ↗
54. 10.1021/acs.iecr.6b0241410.1021/acs.iecr.6b02414 ↗
55. 10.1126/science.aai862510.1126/science.aai8625 ↗
56. 10.1038/srep3325210.1038/srep33252 ↗