Magnetoresistance Characteristics of Magnetic Tunnel Junctions Consisting of Amorphous CoNbZr Alloys for Under and Capping Layers

Magnetic tunnel junctions (MTJs) comprising amorphous CoNbZr layers have been investigated. $Co_85.5Nb_8Zr_6.5$(in at. %) layers were employed to substitute the traditionally used Ta layers with an emphasis given on under-standing underlayer effect. The typical junction structure was $SiO_2/CoNbZr$ or Ta 2/CoFe 8/IrMn 7.5/CoFe 3/Al 1.6 + oxidation/CoFe 3/CoNbZr or Ta 2 (nm). For both as-deposited state and after annealing, the CoNbZr-underlayered structure showed superior surface smoothness up to the tunnel barrier than Ta-underlayerd one (rms roughness of 0.16 vs. 0.34 nm). CoNbZr-based MTJs was proven beneficial for increasing thermal stability and increasing $V_h$ (the bias voltage where MR ratio becomes half) characteristics than Ta-based MTJs. This is because the CoNbZr-based junctions offer smoother interface structure than the Ta-based one.