Coatings of FeAlCoCuNiV high entropy alloy
Source abstract
Abstract
The coatings of FeAlCoCuNiV high entropy alloy were deposited by direct current magnetron sputtering. The microstructure and the mechanical and the electrochemical properties of the coatings are investigated. The coatings exhibit single FCC solid solution. The thickness of the coatings increases with the increasing deposited time. The hardness and Young's modulus of the coatings are 19.7 and 189 GPa, respectively. All coatings exhibit better electrochemical corrosion resistance than the 201 stainless steel in acidic alkali and salt corrosion mediums.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Intermetallics and Advanced Alloy Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Key Laboratory of Automobile Materials of Ministry of Education and Department of Materials Science and Engineering, Jilin University, Changchun 130025, China
Engineering Training Centre, Jilin University, Changchun 130025, China
Funding
National Foundation of Doctoral Station
References (34)
Show source-provided references
1. 10.1002/adem.20030056710.1002/adem.200300567 ↗
2. 10.1002/adem.20030050710.1002/adem.200300507 ↗
3. 10.1016/j.actamat.2015.07.00410.1016/j.actamat.2015.07.004 ↗
4. 10.1016/j.actamat.2013.09.03710.1016/j.actamat.2013.09.037 ↗
5. 10.1126/science.125458110.1126/science.1254581 ↗
6. 10.1016/j.matchemphys.2014.06.06210.1016/j.matchemphys.2014.06.062 ↗
7. 10.1179/1743284714Y.000000073910.1179/1743284714Y.0000000739 ↗
8. 10.1007/s40195-014-0117-410.1007/s40195-014-0117-4 ↗
9. 10.1007/s11661-014-2644-z10.1007/s11661-014-2644-z ↗
10. 10.1016/j.surfcoat.2014.12.01310.1016/j.surfcoat.2014.12.013 ↗
11. 10.1016/j.jallcom.2013.10.25410.1016/j.jallcom.2013.10.254 ↗
12. 10.1016/j.matchemphys.2010.09.01610.1016/j.matchemphys.2010.09.016 ↗
13. 10.1016/j.matlet.2014.11.01710.1016/j.matlet.2014.11.017 ↗
14. 10.1080/10402004.2015.104414810.1080/10402004.2015.1044148 ↗
15. 10.1179/1743294413Y.000000022610.1179/1743294413Y.0000000226 ↗
16. 10.1179/1743294413Y.000000021110.1179/1743294413Y.0000000211 ↗
17. 10.1016/j.jallcom.2015.06.02510.1016/j.jallcom.2015.06.025 ↗
18. 10.1016/j.tsf.2015.02.07010.1016/j.tsf.2015.02.070 ↗
19. 10.1016/j.tsf.2010.11.03410.1016/j.tsf.2010.11.034 ↗
20. 10.1016/j.tsf.2007.07.10910.1016/j.tsf.2007.07.109 ↗
21. 10.1016/j.surfcoat.2004.08.02310.1016/j.surfcoat.2004.08.023 ↗
22. 10.1016/j.surfcoat.2013.08.06410.1016/j.surfcoat.2013.08.064 ↗
23. 10.1016/j.msea.2006.11.04910.1016/j.msea.2006.11.049 ↗
24. 10.1016/j.corsci.2004.11.00810.1016/j.corsci.2004.11.008 ↗
25. 10.1007/s11664-005-0154-x10.1007/s11664-005-0154-x ↗
26. 10.1016/j.jallcom.2009.06.18210.1016/j.jallcom.2009.06.182 ↗
27. 10.1016/j.matdes.2012.11.00110.1016/j.matdes.2012.11.001 ↗
28. 10.14233/ajchem.2014.1817210.14233/ajchem.2014.18172 ↗
29. 10.1016/j.tsf.2008.01.01910.1016/j.tsf.2008.01.019 ↗
30. 10.1016/j.tsf.2011.11.02510.1016/j.tsf.2011.11.025 ↗
31. 10.1016/j.msea.2006.12.00110.1016/j.msea.2006.12.001 ↗
32. 10.1016/j.tsf.2009.10.14210.1016/j.tsf.2009.10.142 ↗
33. 10.2320/matertrans1989.36.86610.2320/matertrans1989.36.866 ↗
34. 10.1088/0022-3727/27/11/01710.1088/0022-3727/27/11/017 ↗