Effect of Annealing Temperature on Soft Magnetic Properties of Cold Rolled 0.30 mm Thick Fe-6.5wt.%Si Foils

0.30 mm thick and 90 mm wide thin foils made of Fe-6.5wt.%Si alloy were successfully fabricated by traditional rolling. The as-rolled sheets had good shapes and shining metal luster. The effects of annealing temperature on the magnetic properties of the sheets were investigated. Excellent Dc properties ($H_c$: 11.55 A/m, ${\mu}_m$: 23710, and $B_s$: 1.439 T) were obtained at an annealing temperature of 1453 K for 1.5 h. At low frequencies ($\leq$ 1 kHz), heat treatment temperature has little effect on iron loss which remained at the level of 9.8 W/kg. Annealing at 1273 K for 1.5 h is optimum for frequencies above 5 kHz.