journal article·2019-01

Influence of V content on properties of Ti–W–V–N films

Sheng He, Lihua Yu, Hongbo Ju, Yaoxiang Geng, Isaac Asempah, Junhua Xu

Surface Engineering· Volume 35· Issue 1
Publisher page

Abstract

Ti–W–V–N composite films with different vanadium contents were synthesised by multi-target reactive magnetron sputtering. The microstructure, mechanical and tribological properties of Ti–W–V–N films were investigated by X-ray diffraction, scanning electron microscope, high-resolution transmission electron microscopy, nanoindentation and high-temperature ball-on-disc tribometer. The results showed that all the Ti–W–V–N composite films were face-centred cubic (fcc) structure, consisting of fcc-(Ti,W,V)N substitutional solid solution. When the V content ≥21.5 at.-%, the films consisted of fcc-(Ti,W,V)N and fcc-VN. The hardness of the films first increased and then decreased with the maximum value of 32.4 GPa, at 21.5 at.-% V. The test temperature had a significant effect on the tribological properties of Ti–W–V–N film with 21.5 at.-% V, the coefficient of friction (CoF) first increased and then decreased, with a minimum value of 0.304 at 700°C.While the wear rate increased gradually with increasing temperature.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Metal and Thin Film Mechanics · Diamond and Carbon-based Materials Research · Advanced materials and composites

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang, People's Republic of China

Funding

National Natural Science Foundation of China

References (31)

Show source-provided references
1. 10.1007/s10854-015-4093-x10.1007/s10854-015-4093-x ↗
2. 10.1002/adem.20170070010.1002/adem.201700700 ↗
3. 10.3390/coatings709013710.3390/coatings7090137 ↗
4. 10.1179/1743294414Y.000000031710.1179/1743294414Y.0000000317 ↗
5. 10.1016/j.surfcoat.2017.03.05810.1016/j.surfcoat.2017.03.058 ↗
6. 10.1179/1743294414Y.000000031710.1179/1743294414Y.0000000317 ↗
7. Yu LH · Mater Sci Eng Powder Metall · 2014 · 19 · 812
8. 10.1016/j.matchar.2015.08.00510.1016/j.matchar.2015.08.005 ↗
9. 10.1016/j.apsusc.2013.10.11710.1016/j.apsusc.2013.10.117 ↗
10. 10.1016/j.triboint.2013.06.00710.1016/j.triboint.2013.06.007 ↗
11. 10.1016/j.surfcoat.2014.04.04610.1016/j.surfcoat.2014.04.046 ↗
12. 10.1016/j.tsf.2007.06.10410.1016/j.tsf.2007.06.104 ↗
13. 10.1016/j.surfcoat.2003.09.03110.1016/j.surfcoat.2003.09.031 ↗
14. 10.1016/j.surfcoat.2003.09.04110.1016/j.surfcoat.2003.09.041 ↗
15. Hong-Xia HU · Mater Sci Eng Powder Metall · 2014 · 19 · 635
16. 10.1016/j.surfcoat.2006.07.06710.1016/j.surfcoat.2006.07.067 ↗
17. 10.1016/j.wear.2005.02.02510.1016/j.wear.2005.02.025 ↗
18. Cheng G · Surf Coat Technol · 2012 · 108 · 1
19. 10.1016/j.susc.2006.12.01010.1016/j.susc.2006.12.010 ↗
20. Deeleard T · Mater Sci Appl · 2013 · 04 · 556
21. Xu Y · Chin J Mater Res · 2009 · 23 · 264
22. 10.1016/S0008-6223(03)00071-X10.1016/S0008-6223(03)00071-X ↗
23. 10.1016/j.vacuum.2014.08.01010.1016/j.vacuum.2014.08.010 ↗
24. 10.1016/j.ijrmhm.2008.06.00810.1016/j.ijrmhm.2008.06.008 ↗
25. 10.1016/j.vacuum.2017.09.04510.1016/j.vacuum.2017.09.045 ↗
26. 10.1016/j.vacuum.2016.11.00410.1016/j.vacuum.2016.11.004 ↗
27. 10.1016/j.surfcoat.2015.10.06810.1016/j.surfcoat.2015.10.068 ↗
28. 10.4028/www.scientific.net/AMM.392.70210.4028/www.scientific.net/AMM.392.702 ↗
29. 10.1126/science.245.4920.84110.1126/science.245.4920.841 ↗
30. 10.1016/j.surfcoat.2013.04.03410.1016/j.surfcoat.2013.04.034 ↗
31. 10.1016/j.wear.2014.03.00310.1016/j.wear.2014.03.003 ↗