Molybdate-phosphate conversion coatings to protect steel in a simulated concrete pore solution
Source abstract
Abstract
Abstract For the corrosion protection of steel rebars in concrete, five different molybdate-phosphate conversion coatings were prepared, by changing the molybdate-phosphate ratio in the conversion baths. Their composition and morphology were studied with GD-OES, XPS, Raman spectroscopy and SEM-EDX and a schematic representation of their structure is suggested. Further, the corrosion resistance properties of the coatings were evaluated in a simulated concrete pore solution (CPS) containing chlorides, using anodic polarization measurements. Thanks to the elaborated surface analysis their corrosion behaviour could be correlated to their structure. The results show that by altering the molybdate-phosphate ratio the structure and, consequently, the corrosion protection properties change significantly. By optimizing this ratio a twofold protection mechanism could be attained, demonstrating both good barrier properties and consistent with active corrosion protection.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Concrete Corrosion and Durability · Concrete and Cement Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (62)
Show source-provided references
1. Bertolini · 2013 · 475
2. Efficiency of coatings applied on rebars in concrete10.1023/A:1004745831261 ↗
3. Corrosion of epoxy-coated rebar in marine bridges part 1 : a 30-year perspective10.5006/1.3452397 ↗
4. Epoxidharzbeschichtete Bewehrung10.1002/best.201300066 ↗
5. Chloride-ion induced corrosion of galvanized and ordinary steel reinforcement in high-performance concrete10.1016/S0008-8846(98)00090-8 ↗
6. Evaluation of the impact of corrosion of hot-dip galvanized reinforcement on bond strength with concrete. A review10.1016/j.conbuildmat.2016.11.096 ↗
7. Guide for the use of stainless steel reinforcement in concrete structures
8. Electrochemistry and surface chemistry of stainless steels in alkaline media simulating concrete pore solutions10.1016/j.electacta.2008.06.007 ↗
9. The use of inorganic conversion coatings to enhance the corrosion resistance of reinforcement and the bond strength at the rebar/concrete10.1016/j.conbuildmat.2007.12.011 ↗
10. Enhancement of bond strength for epoxy-coated rebar using river sand10.1016/S0950-0618(02)00101-0 ↗
11. Corrosion of epoxy-coated rebar in marine bridges part 2: corrosion in cracked concrete
12. Corrosion of hot-dip galvanized steel reinforcement
13. Corrosion inhibitors for steel in concrete: state-of-the-art report10.1016/j.conbuildmat.2006.10.013 ↗
14. Corrosion inhibitors for steel in concrete
15. Inhibitor evaluation in different simulated concrete pore solution for the protection of steel rebars10.1016/j.conbuildmat.2016.07.115 ↗
16. Passivation studies using group VIA anions. IV. Cathodic redox reactions and film formation10.1179/000705984798273137 ↗
17. Wilcox · 1986
18. Behaviour of molybdate-passivated zinc coated steel exposed to corrosive chloride environments10.1023/A:1026461924663 ↗
19. Oxidising alternative species to chromium VI in zinc galvanised steel surface treatment. Part 1 - a morphological and chemical study10.1016/S0257-8972(98)00464-2 ↗
20. Molybdate/phosphate composite conversion coating on magnesium alloy surface for corrosion protection10.1016/j.apsusc.2008.04.095 ↗
21. Non-chromate conversion coating treatments for electrodeposited zinc-nickel alloys10.1080/00202967.1996.11871128 ↗
22. Molybdate conversion coatings on zinc surfaces10.1016/j.jelechem.2004.07.016 ↗
23. The molybdate-zinc conversion process10.1016/j.corsci.2008.10.019 ↗
24. Corrosion behaviour of molybdate-phosphate-silicate coatings on galvanized steel10.1016/j.corsci.2009.06.037 ↗
25. A comparative study of molybdate/silane composite films on galvanized steel with different treatment processes10.1016/j.surfcoat.2010.07.033 ↗
26. Molybdenumphosphorus compounds based passivator to control corrosion of hot dip galvanized coated rebars exposed in simulated concrete pore solution10.1016/j.surfcoat.2008.03.038 ↗
27. Effect of zinc phosphate chemical conversion coating on corrosion behaviour of mild steel in alkaline medium: protection of rebars in reinforced concrete10.1088/1468-6996/9/4/045009 ↗
28. Phosphate treatment of TMT rebar bundle to avoid early rusting: an option for single step process10.1016/j.surfcoat.2006.02.041 ↗
29. Corrosion, layer formation, and oxide reduction of passive iron in alkalinesolution: a combined electrochemical and surface analytical study10.1021/la00078a003 ↗
30. Greenwood · 1997
31. The molybdenum blue reaction for the determination of orthophosphate revisited: opening the black box10.1016/j.aca.2015.07.030 ↗
32. Mapping the formation areas of giant molybdenum blue clusters: a spectroscopic study10.1039/c2dt30661a ↗
33. Surface pretreatment by phosphate conversion coatings - a review
34. Naumkin
35. Thermo Scientific
36. Biesinger
37. Role of chromate, molybdate and tungstate anions on the inhibition of aluminium in chloride solutions10.1023/A:1017587911095 ↗
38. The characterisation of Ce & Mo-based conversion coatings on Al-alloys: part I10.1016/S0010-938X(96)00088-1 ↗
39. Study of oxidic and reduced alumina-supported molybdate and heptamolybdate species by in situ laser Raman spectroscopy10.1021/j100311a018 ↗
40. Hydrolysis of molybdenum (V1). Ultracentrifugation, acidity measurements, and Raman spectra of polymolybdates10.1021/ic50015a030 ↗
41. Studies on polynuclear molybdates in the aqueous solution by laser Raman spectroscopy10.1016/0584-8539(83)80018-X ↗
42. Studies on yellow and colourless molybdophosphate complexes in the aqueous solution by laser Raman spectroscopy10.1016/S0277-5387(00)81445-X ↗
43. A mechanistic investigation on the formation of molybdophosphate complexes in aqueous solution by the use of laser Raman spectroscopy10.1016/S0277-5387(00)80771-8 ↗
44. Infrared and Raman spectra of MoO3 molybdenum trioxides and MoO3.xH2O molybdenum trioxide hydrates10.1016/0584-8539(94)00247-9 ↗
45. Solution structure of molybdic acid from Raman spectroscopy and DFT analysis10.1016/j.ica.2007.06.025 ↗
46. Raman-spectroscopic measurements of the first dissociation constant of aqueous phosphoric acid solution from 5 to 301 C10.1007/s10953-012-9825-4 ↗
47. A new investigation of aqueous orthophosphoric acid speciation using Raman spectroscopy10.1023/A:1005150400746 ↗
48. Phosphoesterase activity of polyoxomolybdates: diffusion ordered NMR spectroscopy as a tool for obtaining insights into the reactivity of polyoxometalate clusters.10.1039/b802671h ↗
49. Multicomponent polyanions. 39. Speciation in the a H+-MoO42- -HPO42- system as deduced from a combined Emf-31P NMR study10.1021/ic00246a028 ↗
50. Kim · 1994
51. A surface enhanced Raman spectroscopic study of the passive films formed in borate buffer on iron, nickel, chromium and stainless steel10.1016/0010-938X(94)00102-C ↗
52. Raman studies of corrosion films grown on iron and iron-molybdenum (Fe-6Mo) in pitting conditions10.1016/0010-938X(91)90103-V ↗
53. Raman microspectroscopy of some iron oxides and oxyhydroxides10.1002/(SICI)1097-4555(199711)28:11<873::AID-JRS177>3.0.CO;2-B ↗
54. Potential and drawbacks of Raman (micro)spectrometry for the understanding of iron and steel corrosion
55. Raman spectroscopy of iron molybdate catalyst systems: Part I. Preparation of unsupported catalysts10.1016/0304-5102(90)85170-M ↗
56. Methanol selective oxidation to formaldehyde over iron-molybdate catalysts10.1081/CR-200049088 ↗
57. Comparison of UV and visible Raman spectroscopy of bulk metal molybdate and metal vanadate catalysts10.1021/jp053879j ↗
58. Lafuente
59. The development of passivation coatings by cathodic reduction in sodium molybdate solutions10.1016/0010-938X(88)90025-X ↗
60. Observations on chromate conversion coatings from a sol-gel perspective10.1016/S0300-9440(01)00143-6 ↗
61. Chromate conversion coating
62. An EXAFS investigation of molybdate-based conversion coatings10.1023/A:1024911119051 ↗