MOD方法制备Y 0.5 Yb 0.5 BCO薄膜及其性能研究
Source abstract
Abstract
采用低氟金属有机物沉积工艺, 通过将浓度相同的YBCO、YbBCO前驱溶液按1: 1的体积比混合, 使元素Yb部分取代Y, 成功制备了Y 0.5 Yb 0.5 BCO薄膜. 该薄膜成份单一, 具有很好的双轴织构; 薄膜表面平整致密, 没有裂纹和孔洞, 元素分布均匀. 虽然Yb部分取代Y降低了薄膜的临界转变温度( T c ), 但有效提高了薄膜在高场下的场性能, 如在77K, 3T磁场下, Y 0.5 Yb 0.5 BCO薄膜的 J c 值提高了1.26倍. 为了进一步改善薄膜在低场下的性能, 通过在Y 0.5 Yb 0.5 BCO前驱溶液中再加入6 mol%的TaCl 5 , 成功地制备了Ta 5+ 掺杂的Y 0.5 Yb 0.5 BCO薄膜, 提高了薄膜在整个磁场范围内的载流能力.