低温水热法制备ZnS:Co+Cr纳米晶及其光学性能研究
Source abstract
Abstract
采用低温水热法制备出3-巯基丙酸(MPA)修饰的ZnS:Co+Cr纳米晶. 利用X射线衍射仪、粒度分析仪、透射电镜、紫外–可见分光光度计、荧光分光光度计和XPS能谱仪等对ZnS:Co+Cr纳米晶的结构、形貌、粒径分布和发光性能进行了表征. 结果表明: 合成的ZnS:Co+Cr纳米晶有较好的单分散性, 平均粒径为9.3 nm, 均为立方闪锌矿结构; ZnS:Co+Cr纳米晶的吸收边位于320 nm处, 并在728 nm处出现Co 2+ 的特征吸收峰; 当Cr 2+ 浓度为0.75at%, 水热反应温度为160℃时, ZnS:Co+Cr纳米晶PL峰最强; XPS能谱表明Cr 2+ 部分被氧化成Cr 3+ 。