Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 /CoFe 2 O 4 叠层复合陶瓷的制备与磁电耦合效应研究
Source abstract
Abstract
以CoFe 2 O 4 压磁体、掺CuO和CeO 2 助烧剂的压电体Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 为基本叠层材料, 采用界面固相熔融渗透法制备了掺助烧剂Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 -CoFe 2 O 4 叠层复合陶瓷。叠层复合陶瓷的压电压磁相叠层界面结合良好。随着压磁相与压电相厚度比比率的增加, 叠层复合陶瓷的饱和磁致伸缩系数–λ从67×10 -6 增加到134×10 -6 、压电系数 d 33 从340 pC/N逐渐减小到205 pC/N; 磁电耦合系数先增大后减小, 在厚度比为2、外磁场为100 mT时得到最大值3200 mV/(cm·mT)。