Investigation on comfort and water repellant properties of the Rtv-2 (Bi-component room temperature vulcanizing silicone) silicone coated woven fabric

The main goal of the study is to be obtained water repellant properties of woven fabric coated by Bi-Component Room Temperature Vulcanizing Silicone (RTV-2 silicone) and investigate the physical and thermal properties of these fabrics. In addition, the interaction between calendaring, sanforizing processes, which were known as mechanical finishing treatments, and RTV-2 coating application was investigated in terms of fabric physical performance. According to these experimental results, the possibility of the RTV-2 type silicone as alternative to C6 and C8 based fluorocarbon can be discussed. In this experiment, the woven fabric was coated by RTV-2 silicone with two different coating thickness (0.6 mm and 0.8 mm). The effect of the RTV-2 silicone onto woven fabric were examined and enlightened by physical performance and water repellence tests such as contact angle degree and spray rating tests. The results from contact angle degree and spray rating test pointed out that RTV-2 silicone coated fabric had up to 153.27° contact angle degree and ISO 3 (80) spray rating value whereas untreated fabric had 85.81° contact angle degree and 0 spray rating value. Thermal comfort test (ALAMBETA) showed that, thermal capacity value of the fabric decreased from 0.064 mm ² /s to 0.040 mm ² /s after RTV-2 silicone coating. On the other hand, thermal absorptivity value of the fabric increased from 117.25 to 234.95 W.%s/m ² .K which leaded to increase the cold feeling of the fabric after coating RTV-2 silicone regardless of coating thickness and mechanical finishing processes. Photos from the textile surfaces were taken via Field Emission Scanning Electron Microscope (FE-SEM). It was obviously seen surface morphology after coating and mechanical finishing processes. At the end of the study, it was determined that it is possible to say that RTV-2 silicone usage can positively affect water repellant properties of the fabric while thermal comfort and tactile comfort properties is negatively affected. Fabric performance test such as pilling, abrasion resistance and color fastness to washing did not showed any change after RTV-2 silicone coating and mechanical finishing processes. As for the mechanical finishing processes interaction between RTV-2 silicone, it was seen that the RTV-2 silicone was affected by finishing processes.