Enhanced antistatic properties of polyethylene film/polypropylene-coated non-woven fabrics by compound of hot-melt adhesive and polymer antistatic agent

In this paper, the compound hot-melt adhesives were prepared by blending alkyl sulfonate polymer antistatic agent with modified rosin hot-melt adhesive and used for the preparation of polyethylene film/polypropylene-coated non-woven fabrics. The effects of the amount of antistatic agent on the melt viscosity, softening point, and thermal stability of the compounded hot-melt adhesives were studied. Then, the antistatic properties and its washing fastness of the coated non-woven fabrics were tested and analyzed. The results showed that the softening point and the melt viscosity of the hot-melt adhesives decreased after compounding, and the thermal stability of the compound hot-melt adhesives decreased in the high temperature range, which was not affected before 200℃. The surface inductive voltage, half-life, and specific resistance of the coated non-woven fabrics prepared from the compound adhesives decreased gradually with the increase of the amount of the antistatic agent, indicating that the antistatic property of the prepared fabrics was gradually improved. In addition, the fabrics still exhibited antistatic properties after soaping for several times. The influence of compound adhesive on the wettability of fabric surface was consistent with that of antistatic property. Finally, the mechanism of the hot-melt adhesive and antistatic agent compounding technology to improve the antistatic performance of the coated non-woven fabrics was elaborated, and the reason for its excellent soaping durability was also explained.