Novel synthesis of nanoparticles-based back coating flame-retardant materials for historic textile fabrics conservation

Novel flame-retardant back coating layer for historic textile fabrics was developed. Silica nanoparticles originated from agriculture waste rice husk were prepared through one pot thermal method. The morphological and structure properties of nanoparticles were studied. The silica nanoparticles were further impregnated with organic borate producing flame-retardant composite. The obtained composite incorporated with the binder by mechanical mixing providing flame-retardant coating paste. The coating paste spread on the back surface of textile fabrics. Varied compositions of nanoparticles, binder and organic borate were studied in the back coating layer. The flammability, thermal stability and mechanical properties of the blank and treated samples of linen fabrics as an inner support to the historical textiles were investigated. Flame retardancy of the back-coated linen samples has improved achieved high class of flame-retardant textile fabrics of zero rate of burning compared to 80.3 mm/min for blank. The synergistic effect of flame retardancy between nanoparticles and organic borate was investigated. The tensile strength of the flame retardant fabrics was enhanced by 27% and elongation was improved. The effect of industrial aging on the flame retardancy and mechanical properties of flame-retardant back coating textiles was studied.