Soft magnetic composites of carbon fibers decorated with magnetite in an epoxy matrix

The chemical precipitation was used to obtain carbon fibers (CF) with surface modified by magnetite particles (Fe3O4). Processing was carried out by employing up to three subsequent coating stages of ultrasonic treatments. After each sonication stage, the coating was 17, 33, and 47 wt. % of the total weight of the modified fibers. Raman spectroscopy indicates the presence in the coating of a mixture of iron II and III states. As-decorated fibers were used to fabricate composites with an epoxy resin (ED-20) matrix cured with PEPA. The quantity of the carbon fiber filler was of 1, 3, and 6 wt %. At room temperature, the saturation magnetization of the soft magnetic samples was 0.37, 0.83, and 1.72 emu/g for the indicated compositions. Carbon fiber reinforced polymer materials with extra functions such as magnetic in this case, are expected to be useful in applications from the power and energy industries.