Copolymeric nano/microgels ofN-isopropylacrylamide and carboxyalkyl methacrylamides: Effect of methylene chains and the ionization state of the weak acids on size and sensitivity to pH and temperature

ABSTRACT We prepared nano/microgels by precipitation copolymerization of N-isopropylacrylamide (NIPAAm), and one of three different carboxyalkyl methacrylamides [methacryloylamido hexanoic acid (M5), 8-methacryloylamido octanoic acid (M7), and 11-methacryloylamido undecanoic acid (M10)], either in the acid forms or as carboxylates (potassium salts). The hydrodynamic diameter (Dh) of the nano/microgels prepared with the carboxylates was smaller (≈100 nm for M10 copolymers), compared to the size of homopolymeric NIPAAm microgels prepared by dispersion polymerization (around 600 nm), indicating that the carboxylates act as surfactants reducing the size of the seeds during the polymerization process. These materials presented a swollen-shrunken transition temperature (T tr) similar to the T tr of the homopolymeric NIPAAm microgels, without pH sensitivity. On the other hand, the copolymeric microgels prepared from the acid form of the comonomers have a similar or bigger size than NIPAAm microgels. For these copolymers, the T tr can be tuned by the type and proportion of acid comonomer used and present pH sensitivity. This is important for biomedical applications such as positive temperature control release. Polyelectrolyte titration demonstrates that the nano/microgels prepared with the carboxylates behave as hard spheres, while the microgels prepared with the weak acid behave as porous materials.