The preparation, characterization and actuation behavior of polyaniline and cellulose blended electro-active paper

This paper reports polyaniline and cellulose blended electro-active paper (EAPap) that can produce large bending displacement at ambient humidity conditions with long lifetime durability. A novel solution processable polyaniline-p-toluene sulfonate (PANI–PTSA) salt was prepared by an inverted emulsion polymerization technique using benzoyl peroxide and p-toluene sulfonic acid. Cellulose solution prepared by dissolving cotton with lithium chloride/N, N-dimethylacetamide was mixed with the PANI emaraldine salt solution and a cellulose–PANI blended film was obtained. The obtained cellulose–PANI film was characterized by ultraviolet–visible (UV–visible), x-ray diffraction, scanning electron microscopy and tensile test methods. A cellulose–PANI EAPap actuator was made by depositing very thin gold electrodes on both sides of the cellulose–PANI film. When the actuator performance of the cellulose–PANI EAPap was evaluated in terms of bending displacement with respect to the actuation frequencies, voltages and relative humidity levels, a large bending displacement was shown at ambient humidity conditions with long lifetime durability.