Strain effects on the coarsening and softening of electrodeposited nanocrystalline Ni subjected to high pressure torsion
Source abstract
Abstract
The softening of electrodeposited nanocrystalline nickel due to grain coarsening caused by high pressure torsion at room temperature was studied. The extent of coarsening and softening increases with increasing applied strains, indicating that large strains and high stresses are required to induce grain growth in nanocrystalline metals.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Microstructure and mechanical properties · Metal and Thin Film Mechanics · Electrodeposition and Electroless Coatings
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. Koch · Mater. Res. Soc. Bull. · 1999 · 24 · 5410.1557/S0883769400051551 ↗
2. Valiev · Prog. Mater. Sci. · 2000 · 45 · 10310.1016/S0079-6425(99)00007-9 ↗
3. Lu · Mater. Sci. Eng., R · 1996 · 16 · 16110.1016/0927-796X(95)00187-5 ↗
4. Wang · Nature · 2002 · 491 · 91210.1038/nature01133 ↗
5. Ji · Acta Mater. · 2004 · 52 · 538110.1016/j.actamat.2004.07.044 ↗
6. Zhang · Appl. Phys. Lett. · 2004 · 85 · 519710.1063/1.1828213 ↗
7. Zhang · Appl. Phys. Lett. · 2005 · 87 · 1
8. Sansoz · Appl. Phys. Lett. · 2006 · 89 · 11190110.1063/1.2352725 ↗
9. Liao · Appl. Phys. Lett. · 2006 · 88 · 02190910.1063/1.2159088 ↗
10. Agnew · Mater. Sci. Eng., A · 1998 · 244 · 14510.1016/S0921-5093(97)00689-8 ↗
11. Höppel · Philos. Mag. A · 2002 · 82 · 178110.1080/01418610208235689 ↗
12. Schiotz · Mater. Sci. Eng., A · 2004 · 375–377 · 97510.1016/j.msea.2003.10.175 ↗
13. Fan · Scripta Mater. · 2006 · 54 · 213710.1016/j.scriptamat.2006.02.041 ↗
14. Pippan · Adv. Eng. Mater. · 2006 · 8 · 104610.1002/adem.200600133 ↗
15. Yang · Acta Mater. · 2007 · 55 · 84910.1016/j.actamat.2006.09.004 ↗
16. Natter · J. Mater. Res. · 1998 · 13 · 118610.1557/JMR.1998.0169 ↗
17. Wetscher · Mater. Sci. Eng., A · 2005 · 410–411 · 21310.1016/j.msea.2005.08.027 ↗
18. Hall · Proc. Phys. Soc. London · 1951 · B64 · 74710.1088/0370-1301/64/9/303 ↗
19. Petch · J. Iron Steel Inst. · 1953 · 174 · 25
20. Brandstetter · Scripta Mater. · 2008 · 58 · 6110.1016/j.scriptamat.2007.08.042 ↗
21. Wu · Appl. Phys. Lett. · 2007 · 90 · 22191110.1063/1.2745250 ↗
22. Yamakov · Nature Mater. · 2002 · 1 · 110.1038/nmat700 ↗
23. Van Swygenhoven · Science · 2002 · 296 · 6610.1126/science.1071040 ↗
24. Wu · J. Mater. Res. · 2007 · 22 · 224110.1557/jmr.2007.0279 ↗
25. Liao · Appl. Phys. Lett. · 2003 · 83 · 506210.1063/1.1633975 ↗
26. Lu · Science · 2004 · 304 · 42210.1126/science.1092905 ↗
27. Kumar · Acta Mater. · 2003 · 51 · 38710.1016/S1359-6454(02)00421-4 ↗
28. Wu · Scripta Mater. · 2006 · 54 · 168510.1016/j.scriptamat.2005.12.045 ↗
29. Schiotz · Nature · 1998 · 391 · 56110.1038/35328 ↗
30. Shan · Science · 2004 · 305 · 65410.1126/science.1098741 ↗