Modification of the structural and optical properties of commercial ZnO powder by mechanical activation

Mechanical activation was used as a method for modification of the structural and optical properties of commercial ZnO powder. For this purpose zinc oxide powder was mechanically treated by grinding in a high-energy vibro-mill in a continual regime in air up to 300 minutes. Starting and modified ZnO samples were characterized using XRD, BET and TEM measurements. Optical properties of these samples were investigated by Raman and photoluminescence (PL) spectroscopy. The color of commercial ZnO powder was white while mechanically activated ZnO powder was dark yellow, indicating the presence of nonstoichiometry. In the Raman spectra of non-activated sample Raman modes of bulk ZnO were observed, while the spectra of modified samples point out structural and stoichiometric changes. The PL spectra of modified samples excited by 325 and 442 nm lines of a He-Cd laser show great difference with respect to the spectra of the original sample. This study confirms that change in the defect structure of the ZnO crystal lattice introduced by mechanical activation affects the optical properties of this material.