Effect of process parameter on mechanical properties of friction stir welded tailored blanks from aluminium alloy 6181-T4
Source abstract
Abstract
Tailor welded blanks (TWBs) are produced by joining at least two sheets of dissimilar gauge and/or properties to achieve a lighter blank of desired stiffness and strength. In this way, the properties of the blank may be tailored to meet the design requirements of a panel. As in steel structures, cost and weight can be saved when using the TWB concept for aluminium. However, use of aluminium is a concern in the automotive industry because of well documented weldability and reproducibility problems, since relatively minor changes in welding parameters may affect the quality of the weld. Friction stir welding offers an attractive alternative to conventional fusion welding methods because of the excellent properties (particularly ductility), reproducibility, robustness and surface finish obtained. However, the working envelope for friction stir welded tailored blanks has yet to be fully explored. In the present study TWBs of the alloy 6181-T4 in a thickness combination 1 to 2 mm have been produced. The influence of welding parameters and welding tools on the weld quality and mechanical properties has been determined. Satisfactory surface finish with no detrimental effects to the mechanical properties has been observed. Weld efficiencies >90% have been consistently achieved.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Material Properties and Failure Mechanisms · Metallurgical and Alloy Processes · Electromagnetic Effects on Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (24)
Show source-provided references
1. Pohl T. ‘Fertigungsqualität und umformbarkeit laserstrahlgesch-weisster formplatinen aus aluminiumlegierungen’, PhD thesis, Lehrstuhl für Fertigungstechnologie, Friedrich-Alexander-Universitat Erlangen-Nürnberg, Germany, 2002.
2. Dinkel F. ‘Umformbarkeit von aluminium-karosserie-blechen mit neuartigen oberflächen’, PhD thesis, Lehrstuhl für Umformtechnik und Gießereiwesen, Technische Universität München, Germany, 1997.
3. CAFE overview – frequently asked questions, Corporate Average Fuel Economy, available at: www.ita.com.gov/cars/rules/cafe/overview.htm.
4. 10.1016/S0921-5093(99)00653-X10.1016/S0921-5093(99)00653-X ↗
5. ULSAB design, 2004, available at: www.worldautosteel.org/ulsab.
6. Kinsey B. · J. Mater. Manuf · 2001 · 5 · 673
7. 10.1179/13621710110153873010.1179/136217101101538730 ↗
8. Kinsey B., and Cao J.: Proc. 29th North American Manufacturing Research Conf. (NAMRC), Gainsville, FL, USA, May 2001, University of Florida.
9. Benedyk J. C. · Light Met. Age · 2000 · 73
10. Auto/Steel Partnership: ‘Tailor welded blank acceptance guidelines’, Automotive Applications Committee, American Iron and Steel Institute, 1997, available at: www.a-sp.org.
11. Knabe E. ‘Ziehen von blechformteilen aus zusammengeschweißten platinen unterschiedlicher blechdicke und güte (tailored blanks)’, PhD thesis, Institut für Umformtechnik der Universität Stuttgart, Germany, 1997.
12. Hartmann G., Müschborn W., Schneider C., and Simon R. ‘High strength sheet metals and new sheet metal components for the light weight astomative manufacture, New developments on sheet metal formability’, (ed. Klass Siegert); 1996, Germany.
13. Auty T. ‘Laser welded tailored blanks’; 1999, Sheet Metal Industries.
14. Waddell W. · Weld. Met. Fabr · 1995 · 63 · 104
15. 10.1016/S0924-0136(99)00367-210.1016/S0924-0136(99)00367-2 ↗
16. 10.1016/S1471-5317(02)00028-710.1016/S1471-5317(02)00028-7 ↗
17. Naeem M., and Jessett R.: Proc. Int. Conf. on ‘Body engineering’, Detroit, MI, USA, September 1998, The Welding Institute/TWI.
18. von Strombeck A., Sheikhi S., and J. F. dos Santos: Proc. 4th Int. Symp. on ‘Friction stir welding’, Salt Lake City, UT, USA, May 2003, The Welding Institute/TWI.
19. Wallentowitz H. · ATZ Worldwide · 2003
20. Thomas W. M. · EP · 1994 · 480
21. Thomas W. M., and Andrews R. E. ‘High performance tools for friction stir welding’, International patent specification PCT/GB99/01128, 1999.
22. Frigaard O., Grong O., Bjorneklett B., and Midling O. T.: Proc. 1st Int. Symp. on ‘Friction stir welding’, Thousand Oaks, CA, USA, June 1999, The Welding Institute/TWI.
23. Midling O. T., and Rorvik G.: Proc. 1st Int. Symp. on ‘Friction stir welding’, Thousand Oaks, CA, USA, June 1999, The Welding Institute/TWI.
24. Russel M. J., and Shercliff H. R.: Proc. 1st Int. Symp. on ‘Friction stir welding’, Thousand Oaks, CA, USA, June 1999, The Welding Institute/TWI.