Influence of heat input and travel speed on microstructure and mechanical properties of double tandem submerged arc high strength low alloy steel weldments

D.M. Viano, N.U. Ahmed, G.O. Schumann

Publisher page

Abstract

An evaluation is presented of the microstructural characteristics and mechanical properties of welds in 20 mm thickness high strength low alloy steel HSLA 80, of Australian manufacture. In total, nine butt joints were prepared using the double tandem (four wire) submerged arc welding process in which both heat input and travel speed were varied. The inclusion size distribution was determined for selected welds and showed that heat input had a major effect. Colour etching techniques were used to reveal the solidification structure, which in turn correlated with welding parameters. As the heat input increased, the cooling rate decreased resulting in a larger cellular dendritic cell spacing, decreased acicular ferrite content, and coarser acicular ferrite laths. The effect of travel speed on delta ferrite cell spacing and prior austenite grain size was found to be co-dependent on the heat input and the thermal profile resulting from multiple electrode welding. These results show that increased deposition rates can be achieved by increasing the travel speed and current density without sacrificing joint quality.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Microstructure and Mechanical Properties of Steels · Welding Techniques and Residual Stresses · Hydrogen embrittlement and corrosion behaviors in metals

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

CSIRO Manufacturing Science and Technology, PO Box 4, Woodville, SA, 5011, Australia

References (48)

Show source-provided references
1. Smith N. J. · Weld. J · 1989 · 68 · 112s
2. Horii Y. · Nippon Steel Tech. Rep · 1988 · 37 · 1
3. Knight D. E. · Weld. J · 1954 · 33 · 303
4. ‘ASM handbook’, 10th edn, Vol. 6, 1073; 1993, Materials Park, OH, ASM International.
5. Uttrachi G.D. · Weld. J · 1968 · 47 · 475
6. 10.2355/isijinternational1966.26.38710.2355/isijinternational1966.26.387 ↗
7. 10.2355/isijinternational1966.26.40310.2355/isijinternational1966.26.403 ↗
8. Teri K., Nakayama S., and Kiyohara M.: Proc. 3rd Int. Conf. ‘Advances in welding’, Harrogate, UK, May 1974, The Welding Institute, Paper 9.
9. Killing R. · Schweissen Schneiden · 1984 · 36 · 352
10. Killing R. · Schweissen Schneiden · 1984 · 36 · 470
11. Easterling K. ‘Introduction to the physical metallurgy of welding’; 1983, London, Butterworth.
12. 10.1179/imtr.1986.31.1.2710.1179/imtr.1986.31.1.27 ↗
13. Savage W. F. · Weld. World · 1980 · 18 · 89
14. Cochrane R. C., and Kirkwood P. R.: Proc. Int. Conf. ‘Trends in steel and consumables for welding’, London, UK, November 1978, The Welding Institute, Paper 35.
15. Liu S. · Weld. J · 1986 · 65 · 139s
16. Dallam C. B. · Weld. J · 1985 · 64 · 140s
17. 10.1007/BF0072222810.1007/BF00722228 ↗
18. 10.1007/BF0120349810.1007/BF01203498 ↗
19. 10.1007/BF0054036910.1007/BF00540369 ↗
20. 10.1007/BF0054238410.1007/BF00542384 ↗
21. Jesseman R. J. · Weld. J · 1983 · 62 · 321s
22. Gianetto J. A. · Weld. J · 1992 · 71 · 407s
23. 10.1007/BF0266549210.1007/BF02665492 ↗
24. Rorvik G. · Weld. J · 1992 · 71 · 331s
25. Smith R. B.: in ‘ASM handbook’, 10th edn, Vol. 6, 655; 1993, Materials Park, OH, ASM International.
26. Le Pera F. S. · J. Met · 1980 · 32 · 38
27. Oldland P. T. · Weld. J · 1989 · 68 · 158s
28. Weld. World · 1991 · 29 · 160
29. ‘Methods for the determination of grain size in metals’, Australian Standard AS 1733, 1976.
30. 10.1179/mst.1988.4.7.64910.1179/mst.1988.4.7.649 ↗
31. Fullman R. L. · Trans. AIME · 1953 · 197 · 447
32. Underwood E. E. ‘Quantitative stereology’; 1970, London, Addison – Wesley.
33. ‘Steel plate, sheet, or coil, age-hardening alloy, structural, high yield strength (hSLA–80 and HSLA–100)’, American Military Standard MIL–STD–24645, 1990.
34. Ahlblom B., Bergstrom U., Hannerz N. E., and Werlefors I.: Proc. Int. Conf. ‘The effects of residual, impurity, and microalloying elements on weldability and weld properties’, London, UK, November 1983, The Welding Institute, Paper 49.
35. 10.2355/isijinternational1966.26.37910.2355/isijinternational1966.26.379 ↗
36. Ito Y., and Bessyo K. ‘A prediction of welding procedure to avoid heat affected zone cracking’, IIW Document IX– 631–69, International Institute of Welding, 1969.
37. Chalmers B. ‘Principles of solidification’; 1963, New York, NY, Wiley.
38. Rodriques P. E. L. B., and Rogerson J. H.: Proc. Conf. ‘Low carbon steels for the eighties’, Plymouth, UK, March 1977, Institution of Metallurgists, Part IIIB–33.
39. Lanzafame J. N. · Weld. J · 1973 · 52 · 226s
40. Jordan M. F. · Br. Weld. J · 1968 · 15 · 553
41. Ahmed N. U. · Weld. J · 1996 · 75 · 15s
42. Dadian M.: Proc. Int. Conf. on ‘Advances in Welding Technology’, Gatlinburg, TN, USA, May 1986, ASM, 101–117.
43. Evans G. M. · Weld. J · 1982 · 61 · 125s
44. Glover A. G. · Weld. J · 1977 · 56 · 267s
45. Garland J. G. · Met. Constr · 1975 · 7 · 275
46. Garland J. G. · Met. Constr · 1975 · 7 · 320
47. Widgery D. J. · Weld. Inst. Res. Bull · 1975 · 16 · 277
48. Abson D. J., Dolby R. E., and Hart P. H. M.: Proc. Int. Conf. ‘Trends in steel and consumables for welding’, London, UK, November 1978, The Welding Institute, Paper 25.