Instantaneous formation of SiOx nanocomposite for high capacity lithium ion batteries by enhanced disproportionation reaction during plasma spray physical vapor deposition
Source abstract
Abstract
Nanocomposite SiOx particles have been produced by a single step plasma spray physical vapor deposition (PS-PVD) through rapid condensation of SiO vapors and the subsequent disproportionation reaction. Core-shell nanoparticles, in which 15 nm crystalline Si is embedded within the amorphous SiOx matrix, form under typical PS-PVD conditions, while 10 nm amorphous particles are formed when processed with an increased degree of non-equilibrium effect. Addition of CH4 promotes reduction in the oxygen content x of SiOx, and thereby increases the Si volume in a nanocomposite particle. As a result, core-shell nanoparticles with x = 0.46 as anode exhibit increased initial efficiency and the capacity of lithium ion batteries while maintaining cyclability. Furthermore, it is revealed that the disproportionation reaction of SiO is promoted in nanosized particles attaining increased Si diffusivity by two orders of magnitude compared to that in bulk, which facilitates instantaneous composite nanoparticle formation during PS-PVD.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Battery Materials · Advanced Battery Materials and Technologies · Supercapacitor Materials and Fabrication
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Materials Engineering, The University of Tokyo, Hongo, Japan
Shimane Institute for Industrial Technology, Matsue, Japan
Funding
Grant-in-Aid for Scientific Research
References (43)
Show source-provided references
1. 10.1149/1.159691710.1149/1.1596917 ↗
2. 10.1016/j.jpowsour.2006.09.08410.1016/j.jpowsour.2006.09.084 ↗
3. 10.1063/1.349261710.1063/1.3492617 ↗
4. 10.1021/nn204476h10.1021/nn204476h ↗
5. 10.1149/1.151898810.1149/1.1518988 ↗
6. Ng SH · J Phys Chem · 2007 · 111 · 11131
7. 10.1038/nnano.2007.41110.1038/nnano.2007.411 ↗
8. 10.1038/nnano.2014.610.1038/nnano.2014.6 ↗
9. 10.1038/nnano.2012.3510.1038/nnano.2012.35 ↗
10. 10.1038/nmat272510.1038/nmat2725 ↗
11. 10.1149/1.201321010.1149/1.2013210 ↗
12. 10.1149/1.214229510.1149/1.2142295 ↗
13. 10.1039/b923926j10.1039/b923926j ↗
14. 10.1016/S0022-0248(01)01202-710.1016/S0022-0248(01)01202-7 ↗
15. 10.1016/j.elecom.2007.11.03410.1016/j.elecom.2007.11.034 ↗
16. 10.1016/j.jpowsour.2007.03.08110.1016/j.jpowsour.2007.03.081 ↗
17. 10.1016/j.jelechem.2011.08.01010.1016/j.jelechem.2011.08.010 ↗
18. 10.1149/1.279028210.1149/1.2790282 ↗
19. 10.1016/j.jpowsour.2011.01.05310.1016/j.jpowsour.2011.01.053 ↗
20. 10.1149/2.115309jes10.1149/2.115309jes ↗
21. 10.1021/acsnano.5b0316610.1021/acsnano.5b03166 ↗
22. 10.1080/1478643060086304710.1080/14786430600863047 ↗
23. 10.1016/j.elecom.2006.11.01410.1016/j.elecom.2006.11.014 ↗
24. 10.1016/S0378-7753(99)00194-910.1016/S0378-7753(99)00194-9 ↗
25. 10.1149/1.159691810.1149/1.1596918 ↗
26. Elliott JF · 1960
27. 10.1088/1468-6996/15/2/02500610.1088/1468-6996/15/2/025006 ↗
28. 10.1063/1.33207010.1063/1.332070 ↗
29. 10.1361/105996306X9264010.1361/105996306X92640 ↗
30. 10.1063/1.487060010.1063/1.4870600 ↗
31. Kambara M · Encyclopedia of Plasma Technol
32. 10.1007/BF0101615410.1007/BF01016154 ↗
33. Abraham FF · 1974
34. 10.1063/1.173283210.1063/1.1732832 ↗
35. 10.1021/je800560b10.1021/je800560b ↗
36. 10.1063/1.45681210.1063/1.456812 ↗
37. 10.1016/j.jnoncrysol.2003.12.05710.1016/j.jnoncrysol.2003.12.057 ↗
38. 10.1080/0278682900895946110.1080/02786829008959461 ↗
39. 10.1063/1.346422810.1063/1.3464228 ↗
40. 10.1080/0010220710895247110.1080/00102207108952471 ↗
41. 10.1016/j.jcrysgro.2010.12.07310.1016/j.jcrysgro.2010.12.073 ↗
42. 10.1063/1.9584210.1063/1.95842 ↗
43. 10.1016/0502-8205(52)90009-910.1016/0502-8205(52)90009-9 ↗