Tailoring the morphology and crystallinity of poly(L-lactide acid) electrospun membranes
Source abstract
Abstract
Biodegradable poly(L-lactic acid) (PLLA) microfibers were prepared by electrospinning by varying the applied potential, solution flow rate and collector conditions. PLLA fibers with smoothly oriented and random morphologies were obtained and characterized by scanning electron microscopy. The optimum fiber orientation was obtained at 1000 rpm using a 20.3 cm diameter collecting drum, while for higher and lower drum rotation speeds, the rapid random motion of the jets resulted in a random fiber distribution. The deformation of the jet with rapid solidification during electrospinning often results in a metastable phase. PLLA electrospun fibers are amorphous but contain numerous crystal nuclei that rapidly grow when the sample is heated to 70-140 °C. In this way, the degree of crystallinity of the fibers can be tailored between 0 and 50% by annealing. Infrared transmission spectra revealed that the processing conditions do not affect the PLLA samples at the molecular level and that the crystallinity of the samples is related to the presence of α-crystals.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Electrospun Nanofibers in Biomedical Applications · biodegradable polymer synthesis and properties · Advanced Sensor and Energy Harvesting Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Centro/Departamento de Física da Universidade do Minho, Campus de Gualtar, 4710-057 Braga, Portugal
CeNTI - Centre for Nanotechnology and Smart Materials, Rua Fernando Mesquita 2785, 4760-034 Vila Nova de Famalicão, Portugal
Centro de Biomateriales e Ingeniería Tisular, Universidad Politécnica de Valencia, 46022 Valencia, Spain
Centro de Investigación Príncipe Felipe, Autopista del Saler 16, 46013 Valencia, Spain
CIBER en Bioingeniería, Biomateriales y Nanomedicina, Valencia, Spain
References (35)
Show source-provided references
1. Venugopal J · J. Nanoeng. Nanosyst. · 2005 · 218 · 35
2. 10.2174/187476471080101006810.2174/1874764710801010068 ↗
3. 10.1023/A:102020082243510.1023/A:1020200822435 ↗
4. 10.1021/ma802494310.1021/ma8024943 ↗
5. 10.1002/(SICI)1097-4628(19970214)63:7<855::AID-APP5>3.0.CO;2-P10.1002/(SICI)1097-4628(19970214)63:7<855::AID-APP5>3.0.CO;2-P ↗
6. 10.1088/0954-0083/13/2/31710.1088/0954-0083/13/2/317 ↗
7. 10.1177/875608790303970210.1177/8756087903039702 ↗
8. 10.1021/ma071258d10.1021/ma071258d ↗
9. 10.1016/j.polymdegradstab.2009.05.01510.1016/j.polymdegradstab.2009.05.015 ↗
10. 10.1016/j.polymer.2006.05.01210.1016/j.polymer.2006.05.012 ↗
11. 10.1021/bm060786e10.1021/bm060786e ↗
12. 10.1002/masy.20085120910.1002/masy.200851209 ↗
13. 10.1002/mame.20050021510.1002/mame.200500215 ↗
14. Zeng J · e-Polymers · 2003 · 009 · 1
15. 10.1081/MB-12002157010.1081/MB-120021570 ↗
16. 10.1016/S0032-3861(02)00275-610.1016/S0032-3861(02)00275-6 ↗
17. 10.1016/S0266-3538(03)00178-710.1016/S0266-3538(03)00178-7 ↗
18. 10.1021/nl048615810.1021/nl0486158 ↗
19. 10.1016/j.polymer.2006.08.04210.1016/j.polymer.2006.08.042 ↗
20. 10.1002/app.1994.07051021610.1002/app.1994.070510216 ↗
21. 10.1002/mabi.20040009210.1002/mabi.200400092 ↗
22. 10.1002/polb.2045710.1002/polb.20457 ↗
23. 10.1002/app.1991.07043010910.1002/app.1991.070430109 ↗
24. 10.1021/bm050323t10.1021/bm050323t ↗
25. 10.1021/ma071270610.1021/ma0712706 ↗
26. 10.1021/jp048308q10.1021/jp048308q ↗
27. 10.1002/1521-3900(200208)185:1<35::AID-MASY35>3.0.CO;2-F10.1002/1521-3900(200208)185:1<35::AID-MASY35>3.0.CO;2-F ↗
28. 10.1021/ma001602610.1021/ma0016026 ↗
29. 10.1021/ma020364710.1021/ma0203647 ↗
30. 10.1002/mame.20039000610.1002/mame.200390006 ↗
31. 10.1080/1040839090306097010.1080/10408390903060970 ↗
32. 10.1016/S0032-3861(97)00229-210.1016/S0032-3861(97)00229-2 ↗
33. 10.1021/ma051232r10.1021/ma051232r ↗
34. 10.1021/ma800343g10.1021/ma800343g ↗
35. 10.1021/ma049288t10.1021/ma049288t ↗