Internal stress behavior of the short ceramic fiber reinforced aluminum alloy under tensile deformation

The in situ measurement of phase stress under tensile deformation on an A6061 alloy reinforced with SiC whiskers (Al/SiCw MMC: Metal Matrix Composite) was performed using the X-ray diffraction technique. In order to raise a preciseness of measurements, we applied a profile fitting technique to separate the nearby located diffraction peak. Tensile deformation onelastic to plastic range was applied by four points bending device and discussed internal stress behavior in the short ceramic fiber reinforced MMC. Phase stress in Al matrix was increased linearly up to 2800×10–6 in strain and then saturated immediately. On the other hand phase stress in SiC whiskers shows an unstable stress behavior. It was decreased at first because of the Poisson’s effect from Al matrix but reversed over 500×10–6 applied strain. The measured phase stress behavior in elastic region agreed with the calculations using micromechanics based on Eshelby/Mori–Tanaka model except for this unstable internal stress region. The macro stress behavior in plastic region was extremely small than that of the tensile test results. It supposed that the mechanism of strength is not so much the fiber reinforcing as the dispersion strengthening like the Orowan mechanism. Regarding the fatigue property, DKth of the Al/SiC MMC, this was lower than that of the A6061 alloy. On the Al/SiCw MMC specimen, many micro void formations were observed around the fatigue crack tip even under the ΔKth of A6061. It was considered that these were caused by the high gradient of residual stress on composite process and the unstable stress behavior in low ΔK region.