Microstructure and mechanical properties of multi‐principal component AlCoCrFeNiCu x alloy

Jin‐Ming Zhu, Jie‐Li Meng, Jian‐Lie Liang

Rare Metals· Volume 35· Issue 5
Publisher page

Abstract

Abstract By introducing Cu, AlCoCrFeNiCu x ( x values in molar ratio, x = 0, 0.1, 0.5, 1.0, 1.5, 2.0, and 2.5) alloys were designed and prepared. The effects of Cu on microstructure and properties of AlCoCrFeNi alloy were investigated. The introduction of Cu results in the formation of Cu‐rich FCC solid solution phase when Cu content is low. There are two FCC solid solution phases, i.e., Cu‐rich FCC solid solution phase and phase transformation‐induced FCC solid solution phase, when the Cu content is more than 1.0. Both the yield stress and plastic strain of alloy show a turning point when the Cu content is 0.5. Among the seven alloys, Cu 0.5 alloy exhibits the largest yield stress of 1187 MPa and the lowest plastic strain of 16.01 %.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Aluminum Alloy Microstructure Properties · Aluminum Alloys Composites Properties · High Entropy Alloys Studies

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

College of Science Guangxi University for Nationalities 530006 Nanning China

Funding

National Natural Science Foundation of China · National Key Research and Development Program of China · Natural Science Foundation of Guangxi Province

References (33)

Show source-provided references
1. Microstructure and mechanical properties of AlTiFeNiCuCr x high‐entropy alloy with multi‐principal elements
2. 10.1016/j.matchemphys.2009.07.06710.1016/j.matchemphys.2009.07.067 ↗
3. 10.1016/j.matchemphys.2009.05.02510.1016/j.matchemphys.2009.05.025 ↗
4. 10.1016/j.msea.2007.01.12210.1016/j.msea.2007.01.122 ↗
5. 10.1016/j.matchemphys.2005.01.00110.1016/j.matchemphys.2005.01.001 ↗
6. 10.1016/j.msea.2006.12.00110.1016/j.msea.2006.12.001 ↗
7. 10.1016/j.msea.2011.11.06310.1016/j.msea.2011.11.063 ↗
8. 10.1016/j.msea.2011.11.04510.1016/j.msea.2011.11.045 ↗
9. 10.1016/S1006‐7191(08)60092‐710.1016/S1006‐7191(08)60092‐7 ↗
10. 10.1016/j.msea.2008.08.02510.1016/j.msea.2008.08.025 ↗
11. 10.1016/j.intermet.2010.03.03010.1016/j.intermet.2010.03.030 ↗
12. 10.1016/j.msea.2012.03.08010.1016/j.msea.2012.03.080 ↗
13. 10.1016/j.scriptamat.2011.01.02010.1016/j.scriptamat.2011.01.020 ↗
14. 10.1016/S1003‐6326(11)61338‐110.1016/S1003‐6326(11)61338‐1 ↗
15. 10.1016/j.msea.2011.11.04410.1016/j.msea.2011.11.044 ↗
16. 10.1016/j.jallcom.2009.12.18310.1016/j.jallcom.2009.12.183 ↗
17. 10.1016/j.matlet.2006.03.14010.1016/j.matlet.2006.03.140 ↗
18. 10.1016/j.msea.2009.09.01910.1016/j.msea.2009.09.019 ↗
19. 10.1016/j.intermet.2006.08.00510.1016/j.intermet.2006.08.005 ↗
20. 10.1016/j.wear.2005.12.00810.1016/j.wear.2005.12.008 ↗
21. 10.1016/j.jallcom.2009.05.14410.1016/j.jallcom.2009.05.144 ↗
22. 10.1016/j.actamat.2012.06.04610.1016/j.actamat.2012.06.046 ↗
23. 10.1016/j.msea.2008.01.06410.1016/j.msea.2008.01.064 ↗
24. 10.1016/j.proeng.2012.03.04310.1016/j.proeng.2012.03.043 ↗
25. 10.1016/j.msea.2010.07.02810.1016/j.msea.2010.07.028 ↗
26. 10.1016/j.msea.2010.07.04910.1016/j.msea.2010.07.049 ↗
27. 10.1016/j.jallcom.2010.10.04710.1016/j.jallcom.2010.10.047 ↗
28. 10.1063/1.273451710.1063/1.2734517 ↗
29. Boer FR · 2001 · 750
30. 10.1063/1.293869010.1063/1.2938690 ↗
31. Callister WD · 2001 · 89
32. 10.1007/s11661‐005‐0283‐010.1007/s11661‐005‐0283‐0 ↗
33. 10.1002/047002084910.1002/0470020849 ↗