Fabrication and histological evaluation of porous carbonate apatite blocks using disodium hydrogen phosphate crystals as a porogen and phosphatization accelerator

Abstract The porous architecture of artificial bones plays a pivotal role in bone ingrowth. Although salt leaching methods produce predictable porous architectures, their application in the low‐temperature fabrication of ceramics remains a challenge. Carbonate apatite (CO₃Ap) blocks with three ranges of pore sizes: 100–200, 200–400, and 400–600 μm, were fabricated from CaCO₃ blocks with embedded Na₂HPO₄ crystals as a porogen and accelerator for CaCO₃‐to‐CO₃Ap conversion. CaCO₃ blocks were obtained from Ca(OH)₂ compacts with Na₂HPO₄ by CO₂ flow at 100% humidity. When carbonated under 100% water humidity, the dissolution of Na₂HPO₄ and the formation of hydroxyapatite were observed. Using 90% methanol and 10% water were beneficial in avoiding the Na₂HPO₄ consumption and generating the metastable CaCO₃ vaterite, which was rapidly converted into CO₃Ap in a Na₂HPO₄ solution in 7 days. For the histological evaluation, the CO₃Ap blocks were implanted in rabbit femur defects. Four weeks after implantation, new bone was formed at the edges of the blocks. After 12 weeks, new bone was observed in the central areas of the material. Notably, CO₃Ap blocks with pore sizes of 100–200 μm were the most effective, exhibiting approximately 23% new bone area. This study sheds new light on the fabrication of tailored porous blocks and provides a useful guide for designing artificial bones.