Novel processing of bioglass ceramics from silicone resins containing micro‐ and nano‐sized oxide particle fillers
Source abstract
Abstract
Abstract Highly porous scaffolds with composition similar to those of 45S5 and 58S bioglasses were successfully produced by an innovative processing method based on preceramic polymers containing micro‐ and nano‐sized fillers. Silica from the decomposition of the silicone resins reacted with the oxides deriving from the fillers, yielding glass ceramic components after heating at 1000°C. Despite the limited mechanical strength, the obtained samples possessed suitable porous architecture and promising biocompatibility and bioactivity characteristics, as testified by preliminary in vitro tests. © 2013 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 102A: 2502–2510, 2014.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Bone Tissue Engineering Materials · Dental materials and restorations · Dental Implant Techniques and Outcomes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Dipartimento di Ingegneria Industriale University of Padova Via Marzolo, 9 35131 Padova Italy
Dipartimento di Ingegneria Industriale INSTM UdR Roma Tor Vergata, University of Rome “Tor Vergata” Via del Politecnico 1 00133 Rome Italy
Dipartimento di Ingegneria “E. Ferrari” Università degli Studi di Modena e Reggio Emilia Via Vignolese 905 41125 Modena Italy
References (45)
Show source-provided references
1. 10.1002/3527606696.ch5h10.1002/3527606696.ch5h ↗
2. 10.1007/s10856-006-0432-z10.1007/s10856-006-0432-z ↗
3. 10.1179/02670830110151076210.1179/026708301101510762 ↗
4. 10.1016/j.actbio.2011.03.01610.1016/j.actbio.2011.03.016 ↗
5. 10.1016/j.jeurceramsoc.2008.08.00210.1016/j.jeurceramsoc.2008.08.002 ↗
6. 10.1016/j.biomaterials.2003.07.00110.1016/j.biomaterials.2003.07.001 ↗
7. 10.1002/adem.20110024110.1002/adem.201100241 ↗
8. 10.1007/s10856-012-4667-610.1007/s10856-012-4667-6 ↗
9. 10.1016/j.jeurceramsoc.2012.10.00610.1016/j.jeurceramsoc.2012.10.006 ↗
10. 10.2109/jcersj.114.42510.2109/jcersj.114.425 ↗
11. 10.1111/j.1551-2916.2010.03876.x10.1111/j.1551-2916.2010.03876.x ↗
12. 10.1016/j.jeurceramsoc.2011.08.01010.1016/j.jeurceramsoc.2011.08.010 ↗
13. 10.1002/adem.20120020210.1002/adem.201200202 ↗
14. 10.1016/j.ceramint.2010.08.02310.1016/j.ceramint.2010.08.023 ↗
15. Kokubo T · 1991 · 113
16. 10.1007/s10971-009-2006-210.1007/s10971-009-2006-2 ↗
17. 10.1016/j.biomaterials.2005.04.02510.1016/j.biomaterials.2005.04.025 ↗
18. 10.1016/j.jeurceramsoc.2009.04.01310.1016/j.jeurceramsoc.2009.04.013 ↗
19. 10.1016/j.actbio.2006.07.01210.1016/j.actbio.2006.07.012 ↗
20. 10.5618/bio.2011.v1.n1.110.5618/bio.2011.v1.n1.1 ↗
21. 10.1179/17436760522501103410.1179/174367605225011034 ↗
22. 10.1016/j.cossms.2003.09.01210.1016/j.cossms.2003.09.012 ↗
23. 10.1007/s00223000113410.1007/s002230001134 ↗
24. Biology of implant osseointegration
25. 10.1016/S0272-8842(02)00223-710.1016/S0272-8842(02)00223-7 ↗
26. 10.1016/j.actbio.2006.01.00610.1016/j.actbio.2006.01.006 ↗
27. 10.1111/j.1151-2916.1991.tb07132.x10.1111/j.1151-2916.1991.tb07132.x ↗
28. 10.1016/S0142-9612(00)00174-510.1016/S0142-9612(00)00174-5 ↗
29. 10.1016/j.actbio.2009.08.02110.1016/j.actbio.2009.08.021 ↗
30. 10.1111/j.1551-2916.2012.05100.x10.1111/j.1551-2916.2012.05100.x ↗
31. 10.1016/j.biomaterials.2007.02.02810.1016/j.biomaterials.2007.02.028 ↗
32. 10.1021/js960480l10.1021/js960480l ↗
33. 10.1002/jbm.a.3171810.1002/jbm.a.31718 ↗
34. 10.1016/j.ceramint.2011.01.02310.1016/j.ceramint.2011.01.023 ↗
35. 10.1016/j.actbio.2010.04.02210.1016/j.actbio.2010.04.022 ↗
36. 10.1002/jbm.a.3171810.1002/jbm.a.31718 ↗
37. 10.1007/s00223-004-0285-810.1007/s00223-004-0285-8 ↗
38. 10.1016/j.matlet.2011.03.06010.1016/j.matlet.2011.03.060 ↗
39. 10.1007/s10856-006-0111-010.1007/s10856-006-0111-0 ↗
40. 10.1016/j.biomaterials.2006.01.01710.1016/j.biomaterials.2006.01.017 ↗
41. 10.1016/j.biomaterials.2009.01.00810.1016/j.biomaterials.2009.01.008 ↗
42. 10.1016/j.actbio.2010.05.01310.1016/j.actbio.2010.05.013 ↗
43. 10.1002/jbm.124010.1002/jbm.1240 ↗
44. 10.1039/b616539g10.1039/b616539g ↗
45. 10.1177/088532820809679810.1177/0885328208096798 ↗