The Al-rich region of the Al–Mn–Ni alloy system. Part I: Ternary phases at 750–950°C
Source abstract
Abstract
Abstract Ternary phases in the Al-rich region of the Al–Mn–Ni alloy system were studied at 950, 850 and 750 °C. Two new ternary intermetallic compounds were revealed: the φ-phase (Al 5 Co 2 -type, hP26 , P 6 3 / mmc : a = 0.76632(16) and c = 0.78296(15) nm) and the κ-phase (κ-Al 14.4 Cr 3.4 Ni l.1 -type, hP227 , P 6 3 / m : a = 1.7625(10) and c = 1.2516(10) nm). The formation of the O -phase ( Pmmn ; oP650 ; O -Al 77 Cr 14 Pd 9 -type; a = 2.3316(16), b = 1.2424(15) and c = 3.2648(14) nm) was confirmed and its chemical composition as well as thermodynamic stability was specified.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Quasicrystal Structures and Properties · Intermetallics and Advanced Alloy Properties · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. Urban · J. Non-Cryst. Solids · 2004 · 334, 335 · 14310.1016/j.jnoncrysol.2003.11.029 ↗
2. Feuerbacher · Acta Mater. · 2005 · 53 · 383310.1016/j.actamat.2005.04.032 ↗
3. Krajči · Phys. Rev. · 2003 · B68 · 16520210.1103/PhysRevB.68.165202 ↗
4. Heggen · Nat. Mater. · 2010 · 9 · 33210.1038/nmat2713 ↗
5. Dolinsek · J. Appl. Phys. · 2009 · 106 · 04391710.1063/1.3207791 ↗
6. Raynor · J. Inst. Met. · 1944 · 70 · 507
7. Robinson · Acta Crystallogr. · 1954 · 7 · 49410.1107/S0365110X54001570 ↗
8. Li · Philos. Mag. · 1992 · B65 · 52510.1080/13642819208207647 ↗
9. Sastry · Mater. Res. Bull. · 1978 · 13 · 106510.1016/0025-5408(78)90172-1 ↗
10. Van Tendeloo · J. Microsc. · 1988 · 149 · 110.1111/j.1365-2818.1988.tb04558.x ↗
11. Singh · Mater. Sci. Eng. · 1994 · A181–A182 · 75410.1016/0921-5093(94)90732-3 ↗
12. Zhou · Scripta Metall. · 1989 · 23 · 157110.1016/0036-9748(89)90130-0 ↗
13. Li · Sci. Rep. RITU · 1996 · A42 · 213
14. Sun · Philos. Mag. · 1995 · B71 · 7110.1080/01418639508240293 ↗
15. Dovbenko · 2005
16. 1991 · vol. 1 · 948
17. Kainuma · J. Alloy Compd. · 1998 · 269 · 17310.1016/S0925-8388(98)00127-3 ↗
18. 1990 · vol. 2 · 970
19. Taylor · Acta Crystallogr. · 1959 · 12 · 39310.1107/S0365110X59001165 ↗
20. Murray · Metall. Trans. · 1986 · 18A · 385
21. Robinson · Acta Crystallogr. · 1952 · 5 · 39710.1107/S0365110X52001246 ↗
22. Harsta · J. Solid State Chem. · 1987 · 70 · 21010.1016/0022-4596(87)90058-2 ↗
23. Newkirk · Acta Crystallogr. · 1961 · 14 · 53210.1107/S0365110X61001637 ↗
24. S. Balanetskyy, G. Meisterernst, M. Feuerbacher, J. Alloy Compd., in press.
25. Marsh · Acta Crystallogr. · 1998 · B54 · 92510.1107/S0108768198007393 ↗
26. Li · Philos. Mag. · 1997 · A76 · 65710.1080/01418619708214027 ↗
27. Sugiyama · J. Alloy Compd. · 2002 · 342 · 14810.1016/S0925-8388(02)00161-5 ↗
28. Grushko · J. Alloy Compd. · 2006 · 417 · 12110.1016/j.jallcom.2005.09.050 ↗
29. Kreiner · J. Alloy Compd. · 1995 · 221 · 1510.1016/0925-8388(94)01374-8 ↗
30. Uchida · Philos. Mag. · 2001 · 81 · 212110.1080/01418610108217138 ↗
31. Ranganathan · Philos. Mag. Lett. · 2002 · 82 · 1310.1080/09500830110088746 ↗
32. Shoemaker · Acta Crystallogr. · 1989 · B45 · 1310.1107/S0108768188010481 ↗
33. Demange · Mater. Sci. Eng. · 2000 · 294 · 7910.1016/S0921-5093(00)01083-2 ↗
34. Kowalski · J. Alloy Compd. · 2010 · 496 · 12910.1016/j.jallcom.2010.02.033 ↗
35. Sui · Philos. Mag. · 1997 · A75 · 37910.1080/01418619708205148 ↗