Microstructure and mechanical properties of Al–Si–Mg ribbons

Abstract In this study, the effect of the microstructural characteristics on the mechanical properties of rapidly solidified A359-type alloy was analyzed. As a result of the rapid solidification processing by melt-spinning, fine equiaxed cells grains with sizes in the range of 0.4–0.7 μm were observed in the ribbon. Heat treatment of the as melt-spun ribbon showed a growth of the nanosized Si particles from 19 nm to 80 nm (200 °C/12 h) and to 1.72 μm (450 °C/12 h). The improvement in hardness and tensile properties are related to supersaturated α-Al solid solution and to the structural refinement. The decrease in hardness and in the tensile properties after thermal ageing is attributed to Si precipitation and subsequent growth of Si particles. The as melt-spun and after heat treated at 200 °C ribbons exhibited a brittle fracture different of the after heat treated at 450 °C ribbon which showed a ductile fracture surface.