The role of hydrogen in the synthesis of High-entropy alloys and their hydrides

The aim of this work is to study the new newly presented processes of formation of stable hydrides of High-entropy alloys (HEAs) with high hydrogen content. The essence of the proposed method is the sequential use of self-propagating high-temperature synthesis (SHS) method for producing the metal hydrides, followed by the formation of alloys in the hydride cycle (HC) method. Preliminary, the hydrides of three compositions of metal mixtures were synthesized in SHS: 0.2TiH2+0.2ZrH2+0.2HfH2+0.2VH2+0.2NbH2, 0.3TiH2+0.15ZrH2+0.15HfH2+0.2VH2+0.2NbH2 and 0.3TiH2+0.1ZrH2+0.1HfH2+0.2VH2+0.2NbH2+0.1MgH2. From the synthesized mixtures of metal hydrides, the HEAs were produced in HC. The resultant hard alloys Ti0.2Zr0.2Hf0.2V0.2Nb0.2, Ti0.3Zr0.15Hf0.15V0.2Nb0.2 and Ti0.3Zr0.15Hf0.15V0.2Nb0.2Mg0.1 without crushing combusted in Н2 at РH2 = 5-30 atm. in SHS mode. As a result, the hydrides of HEAs (Ti0.2Zr0.2Hf0.2V0.2Nb0.2)Н2.05, (Ti0.3Zr0.15Hf0.15V0.2Nb0.2)H2.05 and (Ti0.3Zr0.1Hf0.1V0.2Nb0.2 Mg0.1)H182 were synthesized with H2 content between 2.17-2.42 wt.% and H/Me = 1.82-2.05. The repeating the hydrogenation-dehydrogenation processes for 1-3 times confirmed the exceptional cyclic stability of hydrides and the reversible high hydrogen storage capacity of the alloys. The regularities and the mechanism of formation of HEAs and their hydrides were elucidated. The applicability of combination of SHS and HC methods was demonstrated as highly applicable for synthesis of solid solutions of BCC structure HEAs and of their hydrogen-rich hydrides was demonstrated. The remarkable advantages of the developed efficient, low-energy consuming, waste-free and safe method for the synthesis of HEAs and their hydrides can be of commercial interest and attractive to industry, given the current needs for the development of renewable energy, in particular, the solid hydrogen storage facilities.