Study on tensile behavior at various temperatures of the Mg-7Gd-5Y-1Nd-2Zn-0.5Zr alloy

Mg-rare earth (RE)-Zn alloys with long-period stacking ordered (LPSO) structure show excellent room temperature, elevated temperature mechanical properties. In this work, microstructure and mechanical properties of Mg-7Gd-5Y-1Nd-2Zn-0.5Zr (wt%) alloy after tensile deformation at various temperatures (room temperature (RT), 250 °C and 300 °C) were investigated. The pre-precipitated alloy exhibited tensile yield strength (TYS) of 149 MPa at room temperature, while it maintained relatively high TYS at 250 °C (154 MPa) and 300 ℃ (123 MPa). The microstructural characterizations revealed that such outstanding heat resistance is mainly attributed to the blocky LPSO structure near the grain boundary; basal plate-like precipitates, twins and kink bands inside the grain. The blocky LPSO structure exhibits a coherent boundary with one α-Mg grain, while being incoherent with other α-Mg grains or the LPSO structure. Cracks primarily occured along the incoherent interface. Basal plate-like precipitates formed during elevated temperature tensile deformation included GP zones, γ`, metastable LPSO building blocks, and fine 14H-LPSO structure. A probable γ-precipitation sequence is supersaturated solid solution → GP zones (ABAB-type) → single LPSO building block (γ`)→ various metastable LPSO building block clusters→ 14H-LPSO (γ). The deformation modes (sliding, twinning, kinking, grain boundary sliding, etc) modified with the tensile temperature increase. dislocations were observed at elevated temperatures. As the temperature of tensile test increases, twins become less. Grain boundary sliding occurs at elevated temperatures.