Near-room-temperature magnetic properties and magnetocaloric effect of polycrystalline and nano-scale manganites Pr(0.65-x)NdxSr0.35MnO3 (x ≤ 0.35)

Here we report investigations of structural, electrical and magnetic properties of bulk and nano-sized Pr _0.65-xNd _xSr _0.35MnO ₃ compounds (x ≤ 0.35). Polycrystalline compounds were produced by solid – state reaction and nanocrystalline samples were obtained by sol–gel method. Analysis of x-ray diffraction patterns revealed a change in lattice structure from ‘ Pbnm’ to ‘ R3c’ symmetry, with diminishing cell volume upon increasing Nd ions substitution for all samples. Optical microscopy was used for bulk surface morphology and transmission electron microscopy was implemented for nano-sized samples. Iodometric titration showed oxygen deficiency for bulk compounds and oxygen excess for nano-sized particles. Measurements of resistivity of bulk samples revealed a single peak at temperatures associated with grain boundary conditions and with ferromagnetic/paramagnetic transition and negative magnetoresistivity. Critical magnetic behavior analysis disclosed that the polycrystalline samples are governed by a tricritical mean field and by 3D Heisenberg models while nanocrystalline samples are governed by a mean field model. Curie temperature T _c values remain in near room temperature range for all bulk compounds; they lower with increasing Nd ions substitution from 295 K for the parent bulk compound to 268 K for x = 0.35. T _c is lowered from 255 K for the parent nano-sized compound in small temperature intervals. All compounds exhibit second-order magnetic phase transitions and relatively high magnetic entropy change, with the highest value of 5.74 J/kgK for x = 0.25 bulk sample in μ˳∆H = 4 T. Strong magnetocaloric effect, stability and the possibility of fine-tuning T _c by Nd ions substitution make the investigated bulk polycrystalline compounds promising for application in magnetic refrigeration. Nano-sized samples possess lower magnetic entropy changes of maximum 2.4 J/kgK in μ˳∆H = 4 T for x = 0.15, but wider effective entropy change temperature ( δT _fwhm) and relative cooling power on par with other manganites, bringing them into the conversation as a viable option in cooling materials.