Structure and bonding in TiNiSi type LaMgSnH intermetallic hydride

Volodymyr A. Yartys, Roman V. Denys, Lev G. Akselrud, Ponniah Vajeeston, Robert Dankelman, Jeroen Plomp, Theresa Block, Rainer Pöttgen, David Wragg, Bruno Guilherme Fischer Eggert, Vasyl Berezovets

Abstract

The work was aimed on reaching a better understanding of the effect of magnesium as a component of the hydride-forming LaMgSn intermetallic compound crystallising with the orthorhombic TiNiSi type of structure on the hydrogenation behaviours, crystal structure and bonding interactions with hydrogen. The LaMgSn structure is significantly expanded as compared to the earlier studied isotypic LaNiSn H storage material (volume expansion of 23%), as a result of a substitution of the smaller Ni atoms by much larger Mg atoms. This significantly affects the chemistry of the interaction of the intermetallic compound with hydrogen because a transition metal, Ni, in replaced by an active hydride-forming metal, Mg. The work involved computational studies of the electronic structure of the intermetallic compound and its hydride, and experimental studies of the hydrogenation behaviour and thermal stability of the formed hydride LaMgSnH, its structural characterisation by SR XRD and neutron powder diffraction, and Mössbauer spectroscopic studies of the stannide and its hydride. These studies showed that in the system LaMgSn-H2 a monohydride LaMgSnH is a thermodynamically favourable hydride composition. PDOS levels show that hydrogen and all constituting elemental metals, La, Mg and Sn, have peaks of electron density in the range between − 6 and − 4 eV indicating their hybridisation. The results show the hybridization of H atoms not only with bonded La and Mg atoms forming H-filled tetrahedra La3Mg, but also with Sn despite its atoms do not have bonding interactions with H. This explains the high stability of the metal substructure which does not disproportionate into the binary hydrides of La and Mg even when heated to 200 °C @ 20 bar H2, but instead forms an insertion type hydride. Formation of the monohydride LaMgSnH (Sp.gr. Pnma; a=8.1628(4); b= 4.5555(3); c= 9.2391(5) Å; V= 343.56(5) Å3) causes a small (1.26%) expansion of the unit cell volume compared to LaMgSn, and mainly proceeds along the [100] direction. Hydrogen absorption-desorption cycle results in a reversible formation of the initial compound LaMgSn, with the peak of hydrogen release occurring in vacuum at 355 °C, which is intermediate between the temperatures for the vacuum decomposition of the dihydrides MgH2 and LaH2. From the combined refinements of the Synchrotron (SR) XRD and Neutron Powder Diffraction (NPD) data, deuterium atoms completely and in an ordered way fill a half of the available La3Mg interstitial sites with metal-H/D distances of Mg-D= 2.026 Å; La-D= 2.381 and 2.502 Å. The occupied La3Mg sites are smaller in size than the vacant Mg3La tetrahedra. Sn and D exhibit a nonbonding interaction with the closest Sn-D separation of 3.033 Å. 119Sn Mössbauer spectra of LaMgSn and LaMgSnH show isomer shifts of 1.98(2) and 1.99(1) mm/s which are typical for the chemically similar stannides.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Rare-earth and actinide compounds · Hydrogen Storage and Materials · Nuclear Materials and Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (49)

Show source-provided references
1. R.-D. Hoffmann, R. Pöttgen, 2001. AlB2 Related Intermetallic Compounds – A Comprehensive View Based on Group-Subgroup Relations, Z. Kristallogr. 216. 127–145.10.1524/zkri.216.3.127.20327 ↗
2. Coloring, distortions and puckering in selected intermetallic structures from the perspective of group-subgroup relations10.1002/zaac.201400023 ↗
3. Chapter 1 - Magnetic phenomena in equiatomic ternary rare earth compounds10.1016/bs.hmm.2023.09.001 ↗
4. Review on magnetic and related properties of RTX compounds10.1016/j.jallcom.2014.08.079 ↗
5. Cerium intermetallics with TiNiSi-type structure
6. Hexagonal LaNiSnD2 with filled ZrBeSi-type structure10.1016/S0925-8388(01)01523-7 ↗
7. The crystal structure of TbNiSiD1.7810.1016/S0925-8388(01)01013-1 ↗
8. Hydrogen induced antiferromagnetism in the Kondo semimetal CeNiSn10.1016/S0925-8388(03)00207-X ↗
9. Orthorhombic NdNiSnD with filled TiNiSi-type structure10.1016/S0925-8388(01)01877-1 ↗
10. Crystal and magnetic structure of TbNiSnD studied by neutron powder diffraction10.1016/j.jmmm.2006.08.043 ↗
11. Hydrogen induced structural phase transformation in ScNiSn-based intermetallic hydride characterized by experimental studies and by a theoretical modelling10.1016/j.actamat.2022.118549 ↗
12. The new hydrides CeNiGeH1.6 and CeCuGeH1.0 crystallizing in the derivative hexagonal ZrBeSi-type structure10.1016/j.jssc.2003.09.003 ↗
13. Magnetic ordering induced by the hydrogenation of the ternary stannide CeNiSn10.1016/j.jmmm.2003.11.222 ↗
14. Ordering phenomena in intermetallic CeMX (M=Ni, Cu and X=Si, Ge, Sn) upon hydrogenation10.1016/j.jpcs.2006.01.032 ↗
15. Variations of structure and magnetic properties in UTGe hydrides (T = late transition metal)10.1016/j.jallcom.2011.11.131 ↗
16. Magnetic properties of the hydrogenated unconventional superconductor UCoGe–H10.3139/146.110177 ↗
17. Hydride phases, structure, and magnetic properties of the UNiAlHy system10.1103/PhysRevB.63.094414 ↗
18. On the RMgSn rare earth compounds10.1016/j.jallcom.2009.03.178 ↗
19. Thermal desorption spectroscopy studies of hydrogen desorption from rare earth metal trihydrides REH3 (RE = Dy, Ho, Er)10.1016/j.jallcom.2020.155530 ↗
20. A new multipurpose diffractometer PILATUS@SNBL10.1107/S1600577516002411 ↗
21. Design and performance of a novel neutron powder diffractometer: PEARL at TU Delft10.1107/S160057671601089X ↗
22. WinCSD: software package for crystallographic calculations (Version 4)10.1107/S1600576714001058 ↗
23. R.A. Brand, WinNormos for Igor6 (version for Igor 6.2 or above: 22/02/2017), Universität Duisburg, Duisburg (Germany), 2017.
24. CorelDRAW Graphics Suite 2017 (version 19.0.0.328), Corel Corporation: Ottawa, Ontario (Canada), 2017.
25. G. Kresse, M. Marsman, J. Furthmüller. Vienna Ab-Initio Package Vienna Simulation: VASP the GUIDE; VASP Man, 2014; p 237. https://www.yumpu.com/user/cms.mpi.univie.ac.at.
26. Performance of the Vienna ab initio simulation package (VASP) in chemical applications10.1016/S0166-1280(02)00733-9 ↗
27. Inhomogeneous electron gas10.1103/PhysRev.136.B864 ↗
28. Self-consistent equations including exchange and correlation effects10.1103/PhysRev.140.A1133 ↗
29. Generalized gradient approximation made simple10.1103/PhysRevLett.77.3865 ↗
30. From ultrasoft pseudopotentials to the projector augmented-wave method10.1103/PhysRevB.59.1758 ↗
31. Projector augmented-wave method10.1103/PhysRevB.50.17953 ↗
32. P. Vajeeston, P. Ravindran, C. Ravi, R. Asokamani, 2001. Phys. Rev. B 63 045115. https://doi.org/10.1103/PhysRevB.63.045115.10.1103/PhysRevB.63.045115 ↗
33. V.A. Yartys, R.V. Denys, J.P. Maehlen, C.J. Webb, E.MacA.. Gray, T. Blach, A.A. Poletaev, J.K. Solberg, O. Isnard. Nanostructured Metal Hydrides for Hydrogen Storage Studied by In Situ Synchrotron and Neutron Diffraction, in In-Situ and Operando Probing of Energy Materials at Multiscale Down to Single Atomic Column—The Power of X-Rays, Neutrons and Electron Microscopy, edited by C.M. Wang, N. de Jonge, R.E. Dunin-Borkowski, A. Braun, J-H. Guo, H. Schober, R.E. Winans (Mater. Res. Soc. Symp. Proc. Volume 1262, Warrendale, PA, 2010), Paper #: 1262-W04–01. https://doi.org/10.1557/PROC-1262-W04–01. ISBN: 978–1-60511–239-8.10.1557/PROC-1262-W04-01 ↗
34. In situ synchrotron X-ray diffraction studies of hydrogen desorption and absorption properties of Mg and Mg-Mm-Ni after reactive ball milling in hydrogen10.1016/j.actamat.2009.05.004 ↗
35. Interplay between Kondo and magnetic interactions in Pr0.75Gd0.25ScGeH10.1016/j.jallcom.2023.171351 ↗
36. Stannides and intermetallic tin compounds – fundamentals and applications
37. New Stannides CaTSn2 (T = Rh, Pd, Ir) and Ca2Pt3Sn5 – synthesis, structure, and chemical bonding
38. 119Sn Mössbauer spectroscopy studies of hydrides deriving from the stannide CeNiSn10.1016/j.solidstatesciences.2004.03.008 ↗
39. Hydrogenation of the intermediate valence ternary stannides CeRhSn and CeIrSn10.1016/j.solidstatesciences.2006.02.047 ↗
40. The Doniach diagram and hydrogenation of the ternary compounds CePdIn and CePdSn
41. B. Chevalier, R. Decourt, B. Heying, F.M. Schappacher, U.Ch. Rodewald, R. D. Hoffmann, R. Pöttgen, R. Eger, A. Simon, Inducing magnetism in the Kondo semiconductor CeRhSb through hydrogenation – antiferromagnetic behaviour of the new hydride CeRhSbH0.2. Chem. Mater. 19 (2007) 28–35. https://doi.org/10.1021/cm062168a.10.1021/cm062168a ↗
42. Neutron diffraction studies of Zr-containing intermetallic hydrides with ordered hydrogen sublattice I. Crystal structure of Zr2FeD510.1016/S0925-8388(98)00593-3 ↗
43. Hydrogen ordering and H-induced phase transformations in Zr-based intermetallic hydrides10.1016/S0925-8388(99)00304-7 ↗
44. Neutron diffraction studies of Zr-containing intermetallic hydrides with ordered hydrogen sublattice. II. Orthorhombic Zr3FeD6.7 with filled Re3B-type structure10.1016/S0925-8388(98)00592-1 ↗
45. Rapid solid-state transformation of tetrahedral [AlH4]− into octahedral [AlH6]3− in lithium aluminohydride10.1039/b004144k ↗
46. Solid state phase transformations in LiAlH4 during high-energy ball-milling10.1016/S0925-8388(00)01201-9 ↗
47. Dry mechanochemical synthesis of alane from LiH and AlCl310.1039/C3FD00161J ↗
48. Mechanochemical reactions and hydrogen storage capacities in MBH4–SiS2 systems (M= Li or Na)10.1016/j.ijhydene.2019.01.211 ↗
49. Thermochemical transformations in 2MNH2–3MgH2 systems (M= Li or Na)10.1016/j.ijhydene.2010.02.104 ↗