Triclinic elastic constants for low albite

The full set of elastic constants for plagioclase end-member phase albite (NaAlSi3O8) is reported for the first time. Velocities of surface acoustic waves (both Rayleigh and pseudo-surface waves) were measured using impulsively stimulated light scattering on polished surfaces having six different orientations (three normal to the Cartesian axes and three lying on diagonals). Data were inverted and results tested using several non-linear optimization techniques. Compliance moduli determined under hydrostatic compression provided additional constraints and reduced covariance in the reported constants. The Cartesian coordinate system associated with the constants (using the $$ {\text{C}}\ifmmode\expandafter\bar\else\expandafter\=\fi{1} $$ unit cell) has the y-axis parallel to the crystal b axis, the x-axis parallel to a* (perpendicular to b and c) and the z-axis consistent with a right-handed coordinate system. The values of the moduli C11, C12, C13, C14, C15, C16, C22, C23, C24, C25, C26, C33, C34, C35, C36, C44, C45, C46, C55, C56, C66 and their 2σ uncertainties (in parentheses) are, respectively, 69.1(0.6), 34.0(0.7), 30.8(0.5), 5.1(0.1), −2.4(0.1), −0.9(0.1), 183.5(2.7), 5.5(2.2), −3.9(0.5), −7.7(0.7), −5.8(0.7), 179.5(2.3), −8.7(0.4), 7.1(0.6), −9.8(0.6), 24.9(0.1), −2.4(0.1), −7.2(0.1), 26.8 (0.2), 0.5(0.1), 33.5(0.2). These constants differ significantly from the previously reported pseudo-monoclinic constants that were based on velocity measurements on polysynthetic twinned crystal aggregates. Differences are consistent with systematic errors in the earlier study associated with sparse data and the presence of cracks and other imperfections.