Effect of impurity oxygen concentration on the thermoelectric properties of hot-pressed Zn4Sb3

Abstract Two kinds of thermoelectric p-type semiconductive ɛ-Zn 4 Sb 3 with different oxygen content were prepared by hot-pressing at 748 K under 49 MPa for 5 h in vacuum, and their transport and thermoelectric properties were evaluated to study the effect of oxygen concentration. The oxygen content of Zn 4 Sb 3 fabricated from high-purity Zn and Sb powders and from a commercially available powder was 0.209% and 0.625%, respectively. Electrical resistance and Seebeck coefficient were evaluated from 323 to 673 K. The electrical resistance of the two Zn 4 Sb 3 samples exhibited a similar linear temperature dependence from room temperature up to about 600 K, except that the resistance of the oxygen-poor Zn 4 Sb 3 was slightly higher. Above 600 K, however, the oxygen-rich Zn 4 Sb 3 showed an irregular downward deviation from linearity, unlike the high-purity sample. This anomalous temperature dependence was examined on the basis of the thermal stability of Zn 4 Sb 3 , and could be explained through a mechanism of Zn release and absorption by the Zn 4 Sb 3 lattice at higher temperatures. The Seebeck coefficient showed a temperature dependence similar to that of the electrical resistance, but its absolute value was higher in the case of the oxygen-poor Zn 4 Sb 3 . Based on these electrical properties, it was found that the power factor of the oxygen-poor Zn 4 Sb 3 was about 20% higher. On the other hand, the thermal conductivity of the oxygen-poor Zn 4 Sb 3 was higher. Thus, the thermoelectric performance, i.e., the ZT value, of the oxygen-poor Zn 4 Sb 3 was lower at temperatures above 500 K. The oxygen-poor and oxygen-rich compounds attained their maximum ZT maxima (0.93 and 1.08, respectively) at 622 and 660 K, respectively.