An anode-supported hollow fiber solid oxide fuel cell with (Pr0.5Nd0.5)0.7Sr0.3MnO3−δ–YSZ composite cathode

Abstract A NiO–YSZ anode-supported hollow fiber solid oxide fuel cell (HF-SOFC) has been fabricated with stable (Pr 0.5 Nd 0.5 ) 0.7 Sr 0.3 MnO 3− δ –YSZ (PNSM–YSZ) composite cathode. The NiO–YSZ hollow fiber anode was prepared by the immersion-induced phase inversion technique and shows a special asymmetrical structure with long and large finger-like porous structure near the lumen side of the hollow fiber. A thin and dense YSZ electrolyte membrane (about 10 μm) was deposited on the anode by a vacuum-assisted dip-coating process. The performance of the as-prepared HF-SOFC was tested at 600–800 °C with humidified H 2 as fuel and ambient air as the oxidant. The peak power densities of 459, 325 and 172 mW cm −2 can be obtained at 800, 700 and 600 °C, respectively. The good performance at intermediate temperatures indicates promising applications as power sources for portable devices for the prepared YSZ-based micro-tubular SOFCs with PNSM–YSZ composite cathode.